Based on recent literary sources, this survey discusses the effects of main factors influencing the microbial‐induced calcium carbonate precipitation (MICP), including the bacterial species, bacterial concentration, temperature, and pH value. While the MICP technology has been widely adopted to improve rock and soil characteristics, it has excellent development prospects in many other fields. The breakthrough solutions in the MICP technology are improving geotechnical and foundation sand properties, repairing cement‐based materials, using mineralized film mulching to protect cultural relics, enhancing properties of tailings, desert control, and heavy metal environmental restoration, etc., are discussed. The experimental findings prove that MICP can improve the strength, stiffness, liquefaction resistance, erosion resistance, and permeability of geotechnical materials and maintain the good permeability and permeability of the soil and improve the growth environment of plants. It is an environment‐friendly bioengineering technology. Because microbial mineralization involves a series of biochemical and ionic chemical reactions, there are many reaction steps in the solidification process and the solidification effect of MICP is restricted and affected by many factors. The comprehensive analysis and optimization strategy on MICP industrial implementation should account for micro‐ and macro‐scale effects: the type of bacteria, the concentration of bacteria and cementation solutions, ambient temperature, pH value, and other factors directly affect the crystallization type, morphology, and size of calcium carbonate from the microscopic standpoint, while the macro‐scale factors control the rock and soil mineralization. The limitations and prospects of the MICP technology are outlined.

This experimental investigation was conducted to research the properties of polypropylene (PP) fiber-reinforced cemented paste backfill (CPB). The unconfined compressive strength (UCS) of the fiber-reinforced CPB showed a significant improvement with average UCS increase ratios of 141.07%, 57.62% and 63.17% at 3, 7 and 28 days, respectively. The macroscopic failure mode and SEM analysis indicated that fibers prevented the formation of large tensile and shear cracks during the pull-out and pull-off failure modes. A linear fitting function for the UCS at a curing time of 3 days and two polynomial fitting functions for the UCS at curing times of 7 and 28 days were established to characterize the relationship between the UCS of the fiber-reinforced and unreinforced CPB. Moreover, based on composite mechanics, nonlinear models related to the UCS and fiber reinforcement index were obtained. The estimated functions containing the fiber reinforcement index λ, which consists of the fiber content and aspect ratio of fiber, could evaluate the UCS. Furthermore, the fiber reinforcement index λ quantifies the enhancement by the fibers. Both estimation results indicated that the UCS values were estimated accurately at curing times of 3, 7 and 28 days in this study. Additionally, the estimation models could be used to guide the strength design of fiber-reinforced CPB. Besides this, the results showed that fiber-reinforced CPB can be used more widely in mine backfills and meets the requirements of controlled low-strength material (CLSM) for broader applications.