This work reviews an eco-friendly process for producing TiO₂ via colloidal aqueous sol–gel synthesis, resulting in crystalline materials without a calcination step. Three types of colloidal aqueous TiO₂ are reviewed: the as-synthesized type obtained directly after synthesis, without any specific treatment; the calcined, obtained after a subsequent calcination step; and the hydrothermal, obtained after a specific autoclave treatment. This eco-friendly process is based on the hydrolysis of a Ti precursor in excess of water, followed by the peptization of the precipitated TiO₂. Compared to classical TiO₂ synthesis, this method results in crystalline TiO₂ nanoparticles without any thermal treatment and uses only small amounts of organic chemicals. Depending on the synthesis parameters, the three crystalline phases of TiO₂ (anatase, brookite, and rutile) can be obtained. The morphology of the nanoparticles can also be tailored by the synthesis parameters. The most important parameter is the peptizing agent. Indeed, depending on its acidic or basic character and also on its amount, it can modulate the crystallinity and morphology of TiO₂. Colloidal aqueous TiO₂ photocatalysts are mainly being used in various photocatalytic reactions for organic pollutant degradation. The as-synthesized materials seem to have equivalent photocatalytic efficiency to the photocatalysts post-treated with thermal treatments and the commercial Evonik Aeroxide P25, which is produced by a high-temperature process. Indeed, as-prepared, the TiO₂ photocatalysts present a high specific surface area and crystalline phases. Emerging applications are also referenced, such as elaborating catalysts for fuel cells, nanocomposite drug delivery systems, or the inkjet printing of microstructures. Only a few works have explored these new properties, giving a lot of potential avenues for studying this eco-friendly TiO₂ synthesis method for innovative implementations.

Since the Industrial Revolution, technological advances have generated enormous emissions of various pollutants affecting all ecosystems. The detection and degradation of pollutants has therefore become a critical issue. More than 59 different remediation technologies have already been developed, such as biological remediation, and physicochemical and electrochemical methods. Among these techniques, advanced oxidation processes (AOPs) have been popularized in the treatment of wastewater. The use of ZnO as a photocatalyst for water remediation has been developing fast in recent years. In this work, the goals are to produce ZnO photocatalysts with different morphologies, by using a green sol-gel process, and to study both the influence of the synthesis parameters on the resulting morphology, and the influence of these different morphologies on the photocatalytic activity, for the degradation of an organic pollutant in water. Multiple morphologies were produced (nanotubes, nanorods, nanospheres), with the same crystalline phase (wurtzite). The most important parameter controlling the shape and size was found to be pH. The photoactivity study on a model of pollutant degradation shows that the resulting activity is mainly governed by the specific surface area of the material. A comparison with a commercial TiO₂ photocatalyst (Evonik P25) showed that the best ZnO produced with this green process can reach similar photoactivity without a calcination step.

Ruthenium nanoparticles supported on carbon black were coated by mesoporous protective silica layers (Ru/CB@SiO₂) with different textural properties (S_BET: 280–390 m²/g, pore diameter: 3.4–5.0 nm) and were tested in the selective hydrogenation of glucose into sorbitol. The influence of key parameters such as the protective layer pore size and the solvent nature were investigated. X-ray photoelectron spectroscopy (XPS) analyses proved that the hydrothermal stability was highly improved in ethanolic solution with low water content (silica loss: 99% in water and 32% in ethanolic solution). In this work, the strong influence of the silica layer pore sizes on the selectivity of the reaction (shifting from 4% to 68% by increasing the pores sizes from 3.4 to 5 nm) was also highlighted. Finally, by adding acidic co-catalyst (CB–SO₃H), sorbitol was obtained directly through the hydrolytic hydrogenation of cellobiose (used as a model molecule of cellulose), demonstrating the high potential of the present methodology to produce active catalysts in biomass transformations.