The content of type I collagen (COL-I) and type III collagen (COL-III) and the ratio between them not only affect the skin elasticity and mechanical strength, but also determine the fibril diameter. In this research, we investigated the age-related changes in COL-I/COL-III ratio with their formed fibril diameter. The experimental result was obtained from high performance liquid chromatography mass spectrometry (HPLC-MS), hydroxyproline determination, picrosirius red staining and transmission electron microscopes (TEM), respectively. The result indicated that the COL-I/COL-III ratio in mouse skin increased with aging. From the 0^th to 9^th week, the COL-I/COLIII ratio increased from 1.3:1 to 4.5:1. From the 9^th to the 18^th week, it remained between 4.5:1 to 4.9:1. The total content of COL-I and COL-III firstly increased and then decreased with aging. The TEM result showed that the fibril diameter increased with aging. From the 0^th to 9^th week, the average fibril diameter increased from 40 nm to 112 nm; From the 9^th to 18^th weeks, it increased from 112 nm to 140 nm. After the 9^th week. The fibril diameter showed obvious uneven distribution. Thus, the COL-I/COLIII ratio was proportional to the fibril diameter, but inversely proportional to the uniformity of fibril diameter.

Cytokine secretion researches have been a main focus of studies among the scientists in the recent decades for its outstanding contribution to clinical diagnostics. Localized surface plasmon resonance (LSPR) technology is one of the conventional methods utilized to analyze these issues, as it could provide fast, label-free and real-time monitoring of biomolecule binding events. However, numerous LSPR-based biosensors in the past are usually utilized to monitor the average performance of cell groups rather than single cells. Meanwhile, the complicated sensor structures will lead to the fabrication and economic budget problems. Thus, in this paper, we report a simple synergistic integration of the cell trapping of microwell chip and gold-capped nanopillar-structured cyclo-olefin-polymer (COP) film for single cell level Interleukin 6 (IL-6) detection. Here, in-situ cytokine secreted from the trapped cell can be directly observed and analyzed through the peak red-shift in the transmittance spectrum. The fabricated device also shows the potential to conduct the real-time monitoring which would greatly help us identify the viability and biological variation of the tested single cell.

Collagen Type V (Col. V) plays an essential role in cell behaviors and has attracted increasing attention in recent years. High-purity Col. V is needed for evaluating its biological properties. In this research, the enzymatic hydrolysis process was combined with ultrafiltration to purify Col. V from the bovine cornea. The purity of Col. V was determined to be above 90% by both sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) and high-performance liquid chromatography methods. The effect of Col. V on cell behaviors was evaluated. The circular dichroism spectroscopy results demonstrated that the extracted Col. V exhibited a complete triple helix structure. SDS-PAGE suggested that the molecular weight of Col. V was 440 kDa. The self-assembly experiment revealed that the proportion of Col. V in the collagen mixture can affect the Col. I fiber diameter. The cell culture results implied that Col. V can inhibit fibroblasts (L929) proliferation. The L929 showed maximum mobility when the addition of Col. V was 30%. Thus, Col. V has the effect of inhibiting L929 proliferation and promoting migration. The high-purity Col. V provides useful information for further understanding its biological implications.