Using TiO₂-15MgAl₂O₄ mixed powder as spray-feed, an electrical-heating coating was successfully fabricated by atmospheric plasma spraying technology. The phase composition, microstructure, and electrical-heating performance of the coating were characterized by XRD, SEM, and cyclic electrification tests, respectively. The coating samples were heat-treated at 350 °C in a hydrogen atmosphere. The results show that TiO₂-15MgAl₂O₄ coating can be heated over 300 °C within 30 m at 55.1 V which preserves heat for a long time. Before heat treatment, the available heating temperature of the coating decreases significantly with electrification cycles. The resistivity of coating rises rapidly during the cyclic electricity test. After hydrogen heat treatment, the electrical-heating property of coatings is significantly enhanced.