For minimizing the transport of antibiotics to groundwater, the migration of antibiotics in soils should be investigated. Soil organic matter can affect the migration of antibiotics. To date, the influence of aromatics and aliphatic content of organic matter on the adsorption of antibiotics has been controversial. To better understand the reaction mechanism of soil organic matter with antibiotics, this study investigated the adsorption of oxytetracycline (OTC) by humus soils (HOS) and their fractions. HOS were sequentially fractionated into four organic fractions, including the removal of dissolved organic matter (HRDOM), removal of minerals (HRM), removal of free fat (HRLF), and nonhydrolyzable organic carbon (HNHC). Moreover, batch experiments revealed that adsorption capacity was ordered by HNHC > HOS > HRDOM > HRLF > HRM. SEM images and N₂ adsorption/desorption isotherms indicate that adsorption capacity is independent of the external structure. However, adsorption capacity is related to the internal structure and composition. Combination analysis with elemental composition and infrared spectroscopy showed that the adsorption capacity of HRM, HRLF, and HNHC had a good positive correlation with aromaticity, but a negative correlation with polarity and hydrophilicity. Additionally, the rule of binding affinity between OTC and functional groups with different properties was summarized as aromatic > polarity > hydrophilic.

The hydrophobicity and anti-fouling properties of materials have important application value in industrial and agricultural production and people’s daily life. To study the relationship between the unit width L₀ of the parabolic hydrophobic material and the hydrophobicity and anti-fouling properties, the rough surface structure of the parabolic with different widths was prepared by grinding with different SiC sandpapers, and further, to obtain hydrophobic materials through chemical oxidation and chemical etching, and modification with stearic acid (SA). The morphology, surface wetting and anti-fouling properties of the modified materials were characterized by SEM and contact angle measurement. The oil–water separation performance and self-cleaning performance of the materials were explored. The surface of the modified copper sheet forms a rough structure similar to a paraboloid. When ground with 1500 grit SiC sandpaper, it is more conducive to increase the hydrophobicity of the copper sheet surface and increase the contact angle of water droplets on the copper surface. Additionally, the self-cleaning and anti-fouling experiments showed that as L₀ decreases, copper sheets were less able to stick to foreign things such as soil, and the better the self-cleaning and anti-fouling performance was. Based on the oil–water separation experiment of copper mesh, the lower L₀ has a higher oil–water separation efficiency. The results showed that material with parabolic morphology has great self-cleaning, anti-fouling, and oil–water separation performance. The smaller the L₀ was, the larger the contact angle and the better hydrophobic performance and self-cleaning performance were.

In order to explore the effects of microstructures of membranes on superhydrophobic properties, it is critical, though, challenging, to study microstructures with different morphologies. In this work, a combination of chemical etching and oxidation was used and some copper meshes were selected for grinding. Two superhydrophobic morphologies could be successfully prepared for oil-water separation: a parabolic morphology and a truncated cone morphology. The surface morphology, chemical composition, and wettability were characterized. The results indicated that the water contact angle and the advancing and receding contact angles of the parabolic morphology were 153.6°, 154.6° ± 1.1°, and 151.5° ± 1.8°, respectively. The water contact angle and the advancing and receding contact angles of the truncated cone morphology were 121.8°, 122.7° ± 1.6°, and 119.6° ± 2.7°, respectively. The separation efficiency of the parabolic morphology for different oil-water mixtures was 97.5%, 97.2%, and 91%. The separation efficiency of the truncated cone morphology was 93.2%, 92%, and 89%. In addition, the values of the deepest heights of pressure resistance of the parabolic and truncated cone morphologies were 21.4 cm of water and 19.6 cm of water, respectively. This shows that the parabolic morphology had good separation efficiency, pressure resistance, and superhydrophobic ability compared with the truncated cone morphology. It illustrates that microstructure is one of the main factors affecting superhydrophobic properties.