The aim of this work was to explore the feasibility of combining hot melt extrusion (HME) with 3D printing (3DP) technology, with a view to producing different shaped tablets which would be otherwise difficult to produce using traditional methods. A filament extruder was used to obtain approx. 4% paracetamol loaded filaments of polyvinyl alcohol with characteristics suitable for use in fused-deposition modelling 3DP. Five different tablet geometries were successfully 3D-printed-cube, pyramid, cylinder, sphere and torus. The printing process did not affect the stability of the drug. Drug release from the tablets was not dependent on the surface area but instead on surface area to volume ratio, indicating the influence that geometrical shape has on drug release. An erosion-mediated process controlled drug release. This work has demonstrated the potential of 3DP to manufacture tablet shapes of different geometries, many of which would be challenging to manufacture by powder compaction.

The aim of this work was to evaluate the suitability of stereolithography (SLA) to fabricate drug-loaded tablets with modified-release characteristics. The SLA printer creates solid objects by using a laser beam to photopolymerise monomers. In this work polyethylene glycol diacrylate (PEGDA) was used as a monomer and diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide was used as a photo-initiator. 4-aminosalicylic acid (4-ASA) and paracetamol (acetaminophen) were selected as model drugs. Tablets were successfully printed and formulations with different properties were fabricated by adding polyethylene glycol 300 (PEG 300) to the printing solution. The loading of paracetamol and 4-ASA in the printed tablets was 5.69% and 5.40% respectively. In a realistic dynamic dissolution simulation of the gastrointestinal tract, drug release from the tablets was dependent on the composition of the formulations, but independent of dissolution pH. In conclusion SLA 3DP technology allows the manufacture of drug loaded tablets with specific extended-release profiles. In the future this technology could become a manufacturing technology for the elaboration of oral dosage forms, for industrial production or even for personalised dose.

The use of fused-filament 3D printing (FF 3DP) to fabricate individual tablets is demonstrated. The technology permits the manufacture of tablets containing drug doses tailored to individual patients, or to fabrication of tablets with specific drug-release profiles. Commercially produced polyvinyl alcohol (PVA) filament was loaded with a model drug (fluorescein) by swelling of the polymer in ethanolic drug solution. A final drug-loading of 0.29% w/w was achieved. Tablets of PVA/fluorescein (10 mm diameter) were printed using a 3D printer. It was found that changing the degree of infill percentage in the printer software varied the weight and volume of the printed tablets. The tablets were mechanically strong and no significant thermal degradation of the active occurred during printing. Dissolution tests were conducted in modified Hank's buffer. The results showed release profiles were dependent on the infill percentage used to print the tablet. The study indicates that FF 3DP has the potential to offer a new solution for fabricating personalized-dose medicines or unit dosage forms with controlled-release profiles. In addition, the low cost of FDM printers means the paradigm of extemporaneous or point-of-use manufacture of personalized-dose tablets is both feasible and attainable.

The aim of this study was to explore the potential of fused-deposition 3-dimensional printing (FDM 3DP) to produce modified-release drug loaded tablets. Two aminosalicylate isomers used in the treatment of inflammatory bowel disease (IBD), 5-aminosalicylic acid (5-ASA, mesalazine) and 4-aminosalicylic acid (4-ASA), were selected as model drugs. Commercially produced polyvinyl alcohol (PVA) filaments were loaded with the drugs in an ethanolic drug solution. A final drug-loading of 0.06% w/w and 0.25% w/w was achieved for the 5-ASA and 4-ASA strands, respectively. 10.5mm diameter tablets of both PVA/4-ASA and PVA/5-ASA were subsequently printed using an FDM 3D printer, and varying the weight and densities of the printed tablets was achieved by selecting the infill percentage in the printer software. The tablets were mechanically strong, and the FDM 3D printing was shown to be an effective process for the manufacture of the drug, 5-ASA. Significant thermal degradation of the active 4-ASA (50%) occurred during printing, however, indicating that the method may not be appropriate for drugs when printing at high temperatures exceeding those of the degradation point. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) of the formulated blends confirmed these findings while highlighting the potential of thermal analytical techniques to anticipate drug degradation issues in the 3D printing process. The results of the dissolution tests conducted in modified Hank's bicarbonate buffer showed that release profiles for both drugs were dependent on both the drug itself and on the infill percentage of the tablet. Our work here demonstrates the potential role of FDM 3DP as an efficient and low-cost alternative method of manufacturing individually tailored oral drug dosage, and also for production of modified-release formulations.