There are extensive studies on electromagnetic radiation (EMR) effects during coal and rock deformation and fracturing processes, but few systematic studies on the EMR features of gas-bearing coal under impact failure circumstances. In order to investigate whether the EMR is affected by the gas (CO₂,CH₄,N₂) sorption, coal type and impact energy, we performed a series of impact loading tests on both briquette coal specimens (BCSs) and raw coal specimens (RCSs) at various pore pressures (0–1.5 MPa). We developed a drop hammer test apparatus to allow impact loading tests on gas-bearing coal, and recorded the EMR signal of the damage of coal simultaneously. The result showed that (i) the amplitude range of the EMR signal generated by the impact damage of the gas-bearing coal is approximately 10–600 mV, with an effective duration time of 3–1500 ms and accumulated energy of 0.1–1000 μJ; (ii) when pore pressure is increased, the maximum amplitude, duration and pulse counts of the EMR decrease accordingly; (iii) the coal powder size and impact energy affect damage features and EMR characteristics, where a higher impact impulse causes more severe damage to coal specimens and (iv) the influence of the presence of adsorptive gas on the EMR signal caused by the destruction of coal bodies has both enhancement and reduction effects. During the early warning assessment of coal and gas outbursts using EMR parameters, not all the waveform parameters are sensitive to coal mine methane, but the significant effect of methane on signal volatility should be considered.

To reduce the thermal runaway risk of lithium-ion batteries, a good thermal management system is critically required. As phase change materials can absorb a lot of heat without the need for extra equipment, they are employed in the thermal management of batteries. The thermal management of a Sanyo 26,650 battery was studied in this work by using different composite phase change materials (CPCMs) at different charge–discharge rates. The thorough analysis on the thermal conductivity of CPCMs and the effect of CPCMs was conducted on the maximum surface temperature while charging and discharging. The findings demonstrate the ability of the composite thermal conductivity filler to increase thermal conductivity. It is increased to 1.307 W/(m K) as the ratio of silica and graphene is 1:1 (CPCM-3). The CPCMs can reduce the surface temperature of the cell, and the cooling effect of CPCM-3 is the most obvious, which can reduce the maximum temperature of the cell surface by 13.7 °C and 19 °C under 2 C and 3 C conditions. It is also found that the risk of thermal runaway of batteries under CPCMs thermal management is effectively reduced, ensuring the safe operation of the battery. This research can assist in the safe application of batteries and the development of new energy sources.