Concrete has low porosity and compact microstructure, and thus can be vulnerable to high temperature, and the increasing application of various types of supplementary cementitious materials (SCMs) in concrete makes its high-temperature resistant behavior more complex. In this study, we investigate the effects of four formulations with typical SCMs combinations of fly ash (FA), ultra-fine fly ash (UFFA) and metakaolin (MK), and study the effects of SCMs combinations on the thermal performance, microstructure, and the crystalline and amorphous phases evolution of concrete subjected to high temperatures. The experimental results showed that at 400 °C, with the addition of 20% FA (wt %), the thermal conductivity of the sample slightly increased to 1.5 W/(m·K). Replacing FA with UFFA can further increase the thermal conductivity to 1.7 W/(m·K). Thermal conductivity of concrete slightly increased at 400 °C and significantly reduced at 800 °C. Further, combined usage of SCMs delayed and reduced micro-cracks of concrete subjected to high temperatures. This study demonstrates the potential of combining the usage of SCMs to promote the high-temperature performance of concrete and explains the micro-mechanism of concrete containing SCMs at high temperatures.

This paper presents the experimental findings of a study on the influence of combining usage of supplementary cementitious materials (SCMs) on the performance of high-strength concrete (HSC) subjected to elevated temperatures. In this study, four types of HSC formulations were prepared: HSC made from cement and fly ash (FA), HSC made from cement and ultra-fine fly ash (UFFA), HSC made from cement and UFFA-metakaolin (MK), and HSC made from cement and FA-UFFA-MK. Mechanical and physical properties of HSC subjected to high temperatures (400, 600, 800, and 1000 °C) were studied. Furthermore, the relation between residual compressive strength and physical properties (loss mass, water absorption, and porosity) of HSC was developed. Results showed that the combined usage of SCMs had limited influence on the early-age strength of HSC, while the 28-d strength had been significantly affected. At 1000 °C, the residual compressive strength retained 18.7 MPa and 23.9 MPa for concretes containing 30% UFFA-5% MK and 10% FA-20% UFFA-5% MK, respectively. The specimen containing FA-UFFA-MK showed the best physical properties when the temperature raised above 600 °C. Combined usage of SCMs (10% FA-20% UFFA-5% MK) showed the lowest mass loss (9.2%), water absorption (10.9%) and porosity (28.6%) at 1000 °C. There was a strongly correlated relation between residual strength and physical properties of HSC exposed to elevated temperatures.

This study proposes a new cement mortar incorporating damping aggregate (DA) and investigates the mechanical properties and damping property of the cement mortar. Four types of DA were prepared, lightweight aggregate presaturated water and three types of polymer emulsion. Further, the effects of polypropylene fiber and rubber powder on the performance of the cement mortar were studied. The experimental results showed that the damping ratio of specimens containing 70% DA was approximately three times higher than that of the reference mortar, with a slight decrease in the mechanical properties. Adding fiber was more effective than rubber powder in improving the damping ratio of the cement mortar, and the optimal dosage of fiber was 0.5%.