Molten chloride salt is recognized as a promising heat transfer and storage medium in concentrating solar power in recent years, but there is a serious lack for thermal property data of molten chloride salts. In this work, local structures and thermal properties for molten chloride salt—including NaCl, MgCl₂, and ZnCl₂—were precisely simulated by Born–Mayer–Huggins (BMH) potential in a rigid ion model (RIM) and a polarizable ion model (PIM). Compared with experimental data, distances between cations, densities, and heat capacities of molten chloride slats calculated from PIM agree remarkably better than those from RIM. The polarization effect brings an extra contribution to screen large repulsive Coulombic interaction of cation–cation, and then it makes shorter distance between cations, larger density and lower heat capacity. For NaCl, MgCl₂, and ZnCl₂, PIM simulation deviations of distances between cations are respectively 3.8%, 3.7%, and 0.3%. The deviations of density and heat capacity for NaCl between PIM simulation and experiments are only 0.6% and 2.2%, and those for MgCl₂ and ZnCl₂ are 0.7–10.7%. As the temperature rises, the distance between cations increases and the structure turns into loose state, so the density and thermal conductivity decrease, while the ionic self-diffusion coefficient increases, which also agree well with the experimental results.

Chloride molten salts have become a potential heat storage material for the design of a new generation of concentrating solar power (CSP) (>700 °C) due to its abundant reserves and low cost. The difficulty of measuring the high-temperature thermal properties of chlorides can be effectively solved by using molecular dynamics simulation. However, it is challenging to get the thermophysical properties of multi-component molten salts containing CaCl₂ due to the lack of Born–Mayer–Huggins (BMH) potential parameters of CaCl₂. Through comparative analysis of the structure and thermal properties of CaCl₂, including density and thermal conductivity, a set of Born–Mayer–Huggins (BMH) potential parameters of CaCl₂ named SP2 is determined in this study. The density, specific heat capacity, and thermal conductivity of nine eutectic molten salts are simulated, including NaCl-CaCl₂, KCl-CaCl₂, NaCl-CaCl₂-MgCl₂, and NaCl-CaCl₂-KCl, and the simulation results are found to be in good agreement with the experimental results. It is also found that the SP2 parameters are able to predict the thermal properties and structure of molten multicomponent chlorides including calcium.