Hydrogen terminations (C–H) confer to diamond layers specific surface properties such as a negative electron affinity and a superficial conductive layer, opening the way to specific functionalization routes. For example, efficient covalent bonding of diazonium salts or of alkene moieties can be performed on hydrogenated diamond thin films, owing to electronic exchanges at the interface. Here, we report on the chemical reactivity of fully hydrogenated High Pressure High Temperature (HPHT) nanodiamonds (H-NDs) towards such grafting, with respect to the reactivity of as-received NDs. Chemical characterizations such as FTIR, XPS analysis and Zeta potential measurements reveal a clear selectivity of such couplings on H-NDs, suggesting that C–H related surface properties remain dominant even on particles at the nanoscale. These results on hydrogenated NDs open up the route to a broad range of new functionalizations for innovative NDs applications development.

We have investigated the early stages of graphitization on detonation nanodiamond during sequential annealing treatments under vacuum using x-ray photoelectron spectroscopy. Two different temperature-dependent regimes were observed. Below 900 \ifmmode^\circ\else\textdegree\fi{}C, the nanodiamond surface reconstructs into graphitic domain but does not alter the diamond core. Above 900 \ifmmode^\circ\else\textdegree\fi{}C, graphitization, i.e., carbon hybridization changes from sp3 to sp2, occurs from the nanodiamond surface toward the diamond core. Graphitization is observed at much lower temperatures on nanodiamonds than on bulk diamond due to the high concentration of structural defects on their surface. These results indicate that low-temperature annealing under vacuum is an efficient method to uncouple surface and bulk graphitization. Hybrid nanocarbons formed in these conditions, constituted of a diamond core with a thin graphitic outer shell, may have interesting catalytic and chemical properties.