High-mobility semiconducting polymers offer the opportunity to develop flexible and large-area electronics for several applications, including wearable, portable and distributed sensors, monitoring and actuating devices. An enabler of this technology is a scalable printing process achieving uniform electrical performances over large area. As opposed to the deposition of highly crystalline films, orientational alignment of polymer chains, albeit commonly achieved by non-scalable/slow bulk alignment schemes, is a more robust approach towards large-area electronics. By combining pre-aggregating solvents for formulating the semiconductor and by adopting a room temperature wired bar-coating technique, here we demonstrate the fast deposition of submonolayers and nanostructured films of a model electron-transporting polymer. Our approach enables directional self-assembling of polymer chains exhibiting large transport anisotropy and a mobility up to 6.4 cm² V⁻¹ s⁻¹, allowing very simple device architectures to operate at 3.3 MHz. Thus, the proposed deposition strategy is exceptionally promising for mass manufacturing of high-performance polymer circuits.

Iron single atom catalysts (Fe SACs) are the best‐known nonprecious metal (NPM) catalysts for the oxygen reduction reaction (ORR) of polymer electrolyte membrane fuel cells (PEMFCs), but their practical application has been constrained by the low Fe SACs loading (<2 wt%). Here, a one‐pot pyrolysis method is reported for the synthesis of iron single atoms on graphene (FeSA‐G) with a high Fe SAC loading of ≈7.7 ± 1.3 wt%. The as‐synthesized FeSA‐G shows an onset potential of 0.950 V and a half‐wave potential of 0.804 V in acid electrolyte for the ORR, similar to that of Pt/C catalysts but with a much higher stability and higher phosphate anion tolerance. High temperature SiO₂ nanoparticle‐doped phosphoric acid/polybenzimidazole (PA/PBI/SiO₂) composite membrane cells utilizing a FeSA‐G cathode with Fe SAC loading of 0.3 mg cm⁻² delivers a peak power density of 325 mW cm⁻² at 230 °C, better than 313 mW cm⁻² obtained on the cell with a Pt/C cathode at a Pt loading of 1 mg cm⁻². The cell with FeSA‐G cathode exhibits superior stability at 230 °C, as compared to that with Pt/C cathode. Our results provide a new approach to developing practical NPM catalysts to replace Pt‐based catalysts for fuel cells.