A software is developed for determining the parameters of the thermal expansion tensor of the crystals of any system by a set of experimental diffraction data received using X-ray, synchrotron and other radiations at various temperatures. An algorithm is realized which allows carrying out all calculations from the experimental determination of the Bragg reflection angles to the calculation of the parameters of the thermal expansion tensor of the crystals, including the orientation of the tensor axes with respect to the crystallographic axes. The drawing of the 3D characteristic surface of the tensor and its 2D sections is also provided. The software is aimed at studying the anisotropy of the thermal expansion of the crystal materials and phase transitions, as well as revealing the mechanism and nature of the thermal behavior of substances.

In the present study, the effect of the chemical and phase composition on the thermal properties of silicon oxide carbides (SiOC) has been investigated. Dense monolithic SiOC materials with various carbon contents were prepared and characterized with respect to their thermal expansion, as well as thermal conductivity. SiOC glass has been shown to exhibit low thermal expansion (e.g., ca. 3.2 × 10⁻⁶ K⁻¹ for a SiOC sample free of segregated carbon) and thermal conductivity (ca. 1.5 W/(m∙K)). Furthermore, it has been observed that the phase separation, which typically occurs in SiOC exposed to temperatures beyond 1000–1200 °C, leads to a decrease of the thermal expansion (i.e., to 1.83 × 10⁻⁶ K⁻¹ for the sample above); whereas the thermal conductivity increases upon phase separation (i.e., to ca. 1.7 W/(m∙K) for the sample mentioned above). Upon adjusting the amount of segregated carbon content in SiOC, its thermal expansion can be tuned; thus, SiOC glass ceramics with carbon contents larger than 10–15 vol % exhibit similar coefficients of thermal expansion to that of the SiOC glass. Increasing the carbon and SiC content in the studied SiOC glass ceramics leads to an increase in their thermal conductivity: SiOC with relatively large carbon and silicon carbides (SiC) volume fractions (i.e., 12–15 and 20–30 vol %, respectively) were shown to possess thermal conductivities in the range from 1.8 to 2.7 W/(m∙K).