Modified ultra-high-molecular-weight polyethylene (UHMWPE) with calcium stearate (CS) and polyethylene wax (PEW) is a feasible method to improve the fluidity of materials because of the tense entanglement network formed by the extremely long molecular chains of UHMWPE, and a modified UHMWPE sheet was fabricated by compression molding technology. A Fourier-transform infrared spectroscopy test found that a new chemical bond was generated at 1097 cm⁻¹ in the materials. Besides, further tests on the thermal, thermomechanical, mechanical, and shape memory properties of the samples were also conducted, which indicates that all properties are affected by the dimension and distribution of crystal regions. Moreover, the experimental results indicate that the addition of PEW and CS can effectively improve the mechanical properties. Additionally, the best comprehensive performance of the samples was obtained at the PEW content of 5 wt % and the CS content of 1 wt %. In addition, the effect of temperature on the shape memory properties of the samples was investigated, and the results indicate that the shape fixity ratio (R_f) and the shape recovery ratio (R_r) can reach 100% at 115 °C and 79% at 100 °C, respectively, which can contribute to the development of UHMWPE-based shape memory polymers.

Ultra-high molecular weight polyethylene (UHMWPE)/high-density polyethylene (HDPE) blend with lower viscosity is more suitable for melt spinning compared to pure UHMWPE; however, the mechanical property of the blend fiber is hard to dramatically improve (the maximum tensile strength of 998.27 MPa). Herein, different content modified-nano-SiO₂ is incorporated to UHMWPE/HDPE blend fiber. After adding 0.5 wt% nano-SiO₂, the tensile strength and initial modulus of UHMWPE/HDPE/nano-SiO₂ fiber are increased to 1211 MPa and 12.81 GPa, respectively, 21.57% and 43.32% higher than that of UHMWPE/HDPE fiber. Meanwhile, the influence of the nano-SiO₂ content on the performance for as-spun filament and fiber are emphatically analyzed. The crystallinity and molecular chain orientation of as-spun filament reduces with the addition of nano-SiO₂. On the contrary, for fiber, the addition of nano-SiO₂ promoted the crystallinity, molecular chain orientation and grain refinement more obvious at a lower content. Furthermore, the possible action mechanism of nano-SiO₂ in the as-spun filament extrusion and fiber hot drawing stage is explained.

The polypropylene (PP)/wood flour (WF) composites were prepared using a co-rotating twin-screw extruder followed by a single-screw extruder foaming system in this paper. Polymers, such as polyolefin elastomer (POE), high-density polyethylene (HDPE) or microcrystalline wax, were blended with PP in the preparation of composites to improve the melt strength. And a cavity transfer mixer was introduced to increase the distribution uniformity of components in composites. Meanwhile, the effect of the polymer blends on the microstructure and mechanical properties of samples was investigated. The experimental results show that the addition of POE and HDPE resulted in the second melting peak in the differential scanning calorimeter (DSC) curves and a great decrease in the cell size was caused by the added POE. However, due to the velocity difference of composites in the die, the shape of bubbles gradually became irregular. Moreover, the impact strength of samples significantly increased by 85% for the added POE and the apparent density decreased by 6.7%. And the minimum Vicat softening temperature of 133.7 °C was obtained when the mass ratio of HDPE to PP was 4/6.

Based on additive manufacturing of wood flour and polyhydroxyalkanoates composites using micro-screw extrusion, device and process parameters were evaluated to achieve a reliable printing. The results show that the anisotropy of samples printed by micro-screw extrusion is less obvious than that of filament extrusion fused deposition modeling. The type of micro-screw, printing speed, layer thickness, and nozzle diameter have significant effects on the performance of printed samples. The linear relationship between the influencing parameters and the screw speed is established, therefore, the performance of printed products can be controlled by the extrusion flow rate related to screw speed.

Due to excellent chemical resistance and impermeability, high-density polyethylene (HDPE) is widely used in petrochemical transportation, product packaging, sports equipment, and marine applications. Yet, with the wide variety of service environments, its mechanical and thermal properties do not meet the demand. In the present study, a compounding cross-linker comprising di-tert-butyl peroxide (DTBP) and triallyl isocyanurate (TAIC) is employed by combining with a two-step preparation process. High-quality cross-linking reactions are achieved for HDPE. In this study, the cross-linking of DTBP is first examined separately. A peak cross-linking degree of 74.7% is achieved, and there is a large improvement in thermal resistance and mechanical properties. Subsequently, the composite cross-linking system of DTBP and TAIC is investigated. The peak cross-linking degree is 82.1% (10% increase compared to DTBP). The peak heat deformation temperature is 80.1 °C (22% increase compared to DTBP). The peak impact strength is 104.73 kJ/m² (207% increase compared to neat HDPE). The flexural strength is 33.6 MPa (22% increase compared to neat HDPE). The results show that this cross-linking system further improves the cross-linking degree, heat resistance, and mechanical properties of HDPE, indicating its potential application in engineering materials for high performance.