The paper examines the impact of selected machining techniques and the semi-finished product technological history on deformations of thin-walled elements made of EN AW-2024 T351 aluminium alloy after milling. The following techniques have been implemented: High Performance Cutting, High Speed Cutting, conventional finishing (CF) and combinations of these techniques. As for the semi-finished product technological history, the rolling direction has been analysed. It has been assumed that it can be relevant in relation to the cutting tool feed direction and, in consequence, exert considerable impact on the stress, as well as deformation following machining. The interest in this issue proceeds from significant challenges faced by the industry, particularly in the aerospace sector. The analysis of results obtained has shown that milling in the direction perpendicular to the rolling direction results in larger deformations than milling in the parallel direction. Additionally, it has been revealed that applying a correctly selected machining technique makes it possible to minimise post-machining deformations of thin-walled elements.

The aim of this paper is to analyse the effect of the selected geometric properties of thin-walled structures on post-machining deformations. In the study, EN AW-7075 T651 and EN AW-6082 T651 aluminium alloys were used to prepare specially designed thin-walled sample elements, i.e., elements with walls arranged in a semi-open and closed structure and with a dimension of 165 × 262 × 50.8 mm consisting of bottom and vertical stiffening walls and so-called ribs with a thickness of 1 mm. The measurements of the absolute deformations of the thin-walled bottom were performed with the use of a Vista coordinate-measuring machine by Zeiss with a PH10 head by Renishaw. Based on the obtained results, it was found that absolute deformation values were higher for walls arranged in a semi-open structure. It is related to a lower rigidity of the tested structure resulting from the lack of a stiffening wall, which is the so-called “rib”. Notwithstanding the geometry of the elements, greater absolute deformation values were recorded following conventional cutting methods. The use of high-speed cutting (HSC) provided positive outcomes in terms of minimising the deformation of thin-walled elements. Additionally, it was found that higher absolute deformations were obtained for EN AW-7075 T651 alloy.

This paper presents the results of tests concerning the value of surface free energy on the basis of measurements of contact angle with measure liquids: distilled water and diiodomethane. The surface of steel-316L samples was modified in an ozone atmosphere, and the concentration of ozone and the...

The purpose of this article is to present energetic properties of surface Ti6Al4V titanium as well as surface EN-AW-2017A(PA6) aluminum alloy layers. Values of surface free energy after selected mechanical operations and ozonation were compared. In addition, the influence of different values of ozone concentration on surface layer energetic activation was analyzed. Dispersive and polar components of surface free energy were of particular concern. Comparative evaluation of shearing strength of Ti6Al4V titanium and EN-AW-2017A(PA6) aluminum alloy single-lap adhesive bonded joints were presented. Results can be used as pro-ecological methods of titanium and aluminum alloys preparing for applications where adhesive phenomenon is important.