Viscose fibers were impregnated with different concentrations of diammonium hydrogen phosphate (DAHP), carbonized, activated, and tested as high-performance electrode materials for supercapacitors. The yield of these activated carbon fibers (ACFs) could be increased by a factor of 14 by using DAHP compared to ACF without impregnation. These specific activation procedures yielded a high specific surface area of more than 2700 m²·g⁻¹ with a pore size distribution (PSD) suitable for use as a supercapacitor electrode. The electrode materials were implemented in symmetric supercapacitors using TEMA BF₄ as electrolyte and cyclic voltammetry measurements showed high specific capacitances of up to 167 F·g⁻¹. Furthermore, the devices showed high energy densities of up to 21.4 W·h·kg⁻¹ and high-power densities of up to 8.7 kW·kg⁻¹. The supercapacitors featured high capacity retention (96%) after 10,000 cycles. These results show that ACFs made of viscose fibers, previously impregnated with DAHP, can be used as high-performance electrodes in supercapacitors for energy storage applications.

Willow bark is a byproduct from forestry and is obtained at an industrial scale. We upcycled this byproduct in a two-step procedure into sustainable electrode materials for symmetrical supercapacitors using organic electrolytes. The procedure employed precarbonization followed by carbonization using different types of KOH activation protocols. The obtained electrode materials had a hierarchically organized pore structure and featured a high specific surface area (>2500 m² g⁻¹) and pore volume (up to 1.48 cm³ g⁻¹). The assembled supercapacitors exhibited capacitances up to 147 F g⁻¹ in organic electrolytes concomitant with excellent cycling performance over 10,000 cycles at 0.6 A g⁻¹ using coin cells. The best materials exhibited a capacity retention of 75% when changing scan rates from 2 to 100 mV s⁻¹.

This study investigates flexible (polyamide 6.6 PA-6.6, polyethylene terephthalate PET, Cu, Al, and Ni foils) and, for comparison, stiff substrates (silicon wafers and glass) differing in, for example, in surface free energy and surface roughness and their ability to host cellulose-based thin films. Trimethylsilyl cellulose (TMSC), a hydrophobic acid-labile cellulose derivative, was deposited on these substrates and subjected to spin coating. For all the synthetic polymer and metal substrates, rather homogenous films were obtained, where the thickness and the roughness of the films correlated with the substrate roughness and its surface free energy. A particular case was the TMSC layer on the copper foil, which exhibited superhydrophobicity caused by the microstructuring of the copper substrate. After the investigation of TMSC film formation, the conversion to cellulose using acidic vapors of HCl was attempted. While for the polymer foils, as well as for glass and silicon, rather homogenous and smooth cellulose films were obtained, for the metal foils, there is a competing reaction between the formation of metal chlorides and the generation of cellulose. We observed particles corresponding to the metal chlorides, while we could not detect any cellulose thin films after HCl treatment of the metal foils as proven by cross-section imaging using scanning electron microscopy (SEM).

Interactions of biomolecules at interfaces are important for a variety of physiological processes. Among these, interactions of lectins with monosaccharides have been investigated extensively in the past, while polysaccharide-lectin interactions have scarcely been investigated. Here, we explore the adsorption of galactomannans (GM) extracted from Prosopis affinis on cellulose thin films determined by a combination of multi-parameter surface plasmon resonance spectroscopy (MP-SPR) and atomic force microscopy (AFM). The galactomannan adsorbs spontaneously on the cellulose surfaces forming monolayer type coverage (0.60 ± 0.20 mg·m⁻²). The interaction of a lectin, Concavalin A (ConA), with these GM rendered cellulose surfaces using MP-SPR has been investigated and the dissociation constant K_D (2.1 ± 0.8 × 10⁻⁸ M) was determined in a range from 3.4 to 27.3 nM. The experiments revealed that the galactose side chains as well as the mannose reducing end of the GM are weakly interacting with the active sites of the lectins, whereas these interactions are potentially amplified by hydrophobic effects between the non-ionic GM and the lectins, thereby leading to an irreversible adsorption.