Raman spectroscopy is a most often used standard technique for characterization of different carbon materials. In this work we present the Raman spectra of polycrystalline diamond layers of different quality, synthesized by Hot Filament Chemical Vapor Deposition method (HF CVD). We show how to use Raman spectroscopy for the analysis of the Raman bands to determine the structure of diamond films as well as the structure of amorphous carbon admixture. Raman spectroscopy has become an important technique for the analysis of CVD diamond films. The first-order diamond Raman peak at ca. 1332 cm⁻¹ is an unambiguous evidence for the presence of diamond phase in the deposited layer. However, the existence of non-diamond carbon components in a CVD diamond layer produces several overlapping peaks in the same wavenumber region as the first order diamond peak. The intensities, wavenumber, full width at half maximum (FWHM) of these bands are dependent on quality of diamond layer which is dependent on the deposition conditions. The aim of the present work is to relate the features of diamond Raman spectra to the features of Raman spectra of non-diamond phase admixture and occurrence of other carbon structures in the obtained diamond thin films.

Biomechanical properties of bone depend on the composition and organization of collagen fibers. In this study, Raman microspectroscopy was employed to determine the content of mineral and organic constituents and orientation of collagen fibers in spongy bone in the human head of femur at the microstructural level. Changes in composition and structure of trabecula were illustrated using Raman spectral mapping. The polarized Raman spectra permit separate analysis of local variations in orientation and composition. The ratios of ν₂PO₄ ³⁻/Amide III, ν₄PO₄ ³⁻/Amide III and ν₁CO₃ ²⁻/ν₂PO₄ ³⁻ are used to describe relative amounts of spongy bone components. The ν₁PO₄ ³⁻/Amide I ratio is quite susceptible to orientation effect and brings information on collagen fibers orientation. The results presented illustrate the versatility of the Raman method in the study of bone tissue. The study permits better understanding of bone physiology and evaluation of the biomechanical properties of bone.

In this article, we present orientation study of metallophthalocyanine (MPcs) (CoPc, ZnPc, CuPc, and MgPc) thin films deposited on silicon substrate. The MPc’s thin layers were obtained by the quasi-molecular beam evaporation. The micro-Raman scattering spectra of MPc’s thin films were investigated in the spectral range 550–1650 cm⁻¹ using 488 nm excitation wavelength. Raman scattering studies were performed at room temperature before and after annealing process. Annealing process of thin layers was carried out at 200 °C for 6 h. From polarized Raman spectra using surface Raman mapping, the information on polymorphic phase of MPc’s layers has been obtained. The chosen Raman modes A_1g and B_1g are connected with different polymorphic phases of MPc (α and β form) thin layers. Moreover, the obtained results showed the influence of the annealing process on the ordering of the molecular structure. Following the annealing process, it was observed arrangement of the thin layers structure being revealed in Raman spectra. The obtained results indicate that the annealing process has a significant influence on the structure of thin layers being under study.

Raman microspectroscopy was used to examine the biochemical composition and molecular structure of extracellular matrix in spongy and subchondral bone collected from patients with clinical and radiological evidence of idiopathic osteoarthritis of the hip and from patients who underwent a femoral neck fracture, as a result of trauma, without previous clinical and radiological evidence of osteoarthritis. The objectives of the study were to determine the levels of mineralization, carbonate accumulation and collagen quality in bone tissue. The subchondral bone from osteoarthritis patients in comparison with control subject is less mineralized due to a decrease in the hydroxyapatite concentration. However, the extent of carbonate accumulation in the apatite crystal lattice increases, most likely due to deficient mineralization. The alpha helix to random coil band area ratio reveals that collagen matrix in subchondral bone is more ordered in osteoarthritis disease. The hydroxyapatite to collagen, carbonate apatite to hydroxyapatite and alpha helix to random coil band area ratios are not significantly changed in the differently loaded sites of femoral head. The significant differences also are not visible in mineral and organic constituents’ content in spongy bone beneath the subchondral bone in osteoarthritis disease.

Graphene devices require electric contacts with metals, particularly with gold. Scanning tunneling spectroscopy studies of electron local density of states performed on mono-, bi-, and trigraphene layer deposited on metallic $\text{Au}/\text{Cr}/{\text{SiO}}_2/\text{Si}$ substrate shows that gold substrate causes the Fermi level shift downwards which means that holes are donated by metal substrate to graphene which becomes $p$ -type doped. These experimental results are in good accordance with recently published density function theory calculations.