Cemented paste backfill (CPB) is a common environmentally friendly mining approach. However, it remains undetermined whether CPB pollutes underground mine water. Tank leaching analysis of a CPB mass in distilled water was performed for 120 d, and water quality was tested in situ for a long-term pollution assessment. Computerized tomography was also used to determine the CPB micro-pore structure and ion-leaching mechanism. The dissolved Zn²⁺, Pb²⁺ and As⁵⁺ concentrations in the leachate peaked at 0.56, 0.11 and 0.066 mg/L, respectively, whereas the Co²⁺ and Cd²⁺ concentrations were lower than the detection limit. The CPB porosity decreased from 46.07% to 40.88% by soaking, and 80% of the pore diameters were less than 13.81 μm. The permeability decreased from 0.8 to 0.5 cm/s, and the quantity, length, and diameter of the permeate channels decreased with soaking. An in-situ survey showed novel selective solidification. The Zn²⁺ concentration in the mine water was 10–20 times that of the background water, and the Pb²⁺ concentration was 2–4 times the regulated value. Although the Pb²⁺ content decreased significantly with mining depth, there remains a serious environmental risk. Mine water pollution can be reduced by adding a solidifying agent for Pb²⁺ and Zn^2+, during CPB preparation.

Paste and thickened tailings (PTT) technology can improve the utilization and management of tailings from processing plants. The pore size distribution (PSD) and microstructure evolution affected by the rake shear in thickening tailings beds are essential to produce a high-density tailings underflow. Continuous thickening and computed tomography (CT) scanning tests were conducted to study the PSD with and without shear. The pore morphology was studied to reveal the shearing-dewatering performance of the tailings bed. The results show that at a flocculant solution concentration of 0.01 wt % and a feed slurry concentration of 10 wt%, the underflow concentration with and without shear can reach 58.5 wt %and 55.8 wt %, respectively. The CT image reconstruction models demonstrated that the porosity of the sheared tailings bed increased with the bed height. When the bed height increased from 2.5 to 10 cm, the porosity increased from 35.1% to 41.9%, the pore fractal dimension increased from the range 1.8–1.95 to the range 2.1–2.15, and the pore quantity decreased by 21.39%. The average pore volume increased with increasing height by 13.93%, 16.57% and 12.07%. The pore structure became more complex with the bed height, and the connectivity between pores increased to form water-flow channels, which were beneficial to the drainage of sealed water.