Mussel Fibers: While it is possible to make strong fibers or threads from organic materials, most suffer from high wear abrasion. Marine mussels attach themselves to rocky seashores using a series of byssal threads. Despite the constant rubbing caused by the motion of the tides, the threads show high wear resistance. Harrington et al. (p. 216 , published online 4 March; see the Perspective by Messersmith ) now find that the threads are protected by a proteinaceous outer cuticle that is rich in the amino acid 3,4-dihydroxyphenylalanine (dopa), which is known to be a strong adhesive. The cuticle is also rich in metal ions, primarily Fe ³⁺ . The dopa-metal crosslinks helped to form the tough outer coating.

The adhesive plaques of Mytilus byssus are investigated increasingly to determine the molecular requirements for wet adhesion. Mfp-2 is the most abundant protein in the plaques, but little is known about its function. Analysis of Mfp-2 films using the surface forces apparatus detected no interaction between films or between a film and bare mica; however, addition of Ca(2+) and Fe(3+) induced significant reversible bridging (work of adhesion W(ad) approximately 0.3 mJ/m(2) to 2.2 mJ/m(2)) between two films at 0.35 m salinity. The strongest observed Fe(3+)-mediated bridging approaches the adhesion of oriented avidin-biotin complexes. Raman microscopy of plaque sections supports the co-localization of Mfp-2 and iron, which interact by forming bis- or tris-DOPA-iron complexes. Mfp-2 adhered strongly to Mfp-5, a DOPA-rich interfacial adhesive protein, but not to another interfacial protein, Mfp-3, which may in fact displace Mfp-2 from mica. In the presence of metal ions or Mfp-5, Mfp-2 adhesion was fully reversible. These results suggest that plaque cohesiveness depends on Mfp-2 complexation of metal ions, particularly Fe(3+) and also by Mfp-2 interaction with Mfp-5 at the plaque-substratum interface.

Biological materials are often based on simple constituents and grown by the principle of self-assembly under ambient conditions. In particular, biomineralization approaches exploit efficient pathways of inorganic material synthesis. There is still a large gap between the complexity of natural systems and the practical utilization of bioinspired formation mechanisms. Here we describe a simple self-assembly route leading to a CaCO₃ microlens array, somewhat reminiscent of the brittlestars' microlenses, with uniform size and focal length, by using a minimum number of components and equipment at ambient conditions. The formation mechanism of the amorphous CaCO₃ microlens arrays was elucidated by confocal Raman spectroscopic imaging to be a two-step growth process mediated by the organic surfactant. CaCO₃ microlens arrays are easy to fabricate, biocompatible and functional in amorphous or more stable crystalline forms. This shows that advanced optical materials can be generated by a simple mineral precipitation.