Polyvinyl alcohol (PVA) is one of the few biodegradable synthetic resins from petroleum-based sources that can alleviate white pollution in the environment. PVA film materials have excellent properties, such as high barrier, high transparency, high toughness, biocompatibility, and adjustable water solubility. However, due to the presence of hydrophilic hydroxyl groups in the side chain of PVA resin, when PVA film is placed in a humid or water environment, swelling or even dissolution will occur, which greatly limits its application. Therefore, it is necessary to modify PVA resin to improve water resistance without reducing other properties and can also impart various functionalities to it, thereby widening the application range. This paper reviews the water-resistant modification methods of polyvinyl alcohol and the application of water-resistant films and provides an outlook on the development trend of PVA water-resistant films.

In today’s world, the problem of “white pollution” is becoming more and more serious, and many countries have paid special attention to this problem, and it has become one of the most important tasks to reduce polymer waste and to protect the environment. Due to the degradability, safety, economy and practicality of biodegradable packaging film materials, biodegradable packaging film materials have become a major trend in the packaging industry to replace traditional packaging film materials, provided that the packaging performance requirements are met. This paper reviews the degradation mechanisms and performance characteristics of biodegradable packaging film materials, such as photodegradation, hydrodegradation, thermo-oxidative degradation and biodegradation, focuses on the research progress of the modification of biodegradable packaging film materials, and summarizes some challenges and bottlenecks of current biodegradable packaging film materials.

The polylactic acid (PLA) resin Ingeo 4032D was selected as the research object. Epoxy soybean oil (ESO) and zeolite (3A molecular sieve) were used as plasticizer and reinforcing filler, respectively, for PLA blend modification. The mixture was granulated in an extruder and then blown to obtain films under different conditions to determine the optimum processing temperatures and screw rotation. Then, the thermal behaviour, crystallinity, optical transparency, micro phase structure and physical properties of the film were investigated. The results showed that with increasing zeolite content, the crystallization behaviour of PLA changed, and the haze of the film increased from 5% to 40% compared to the pure PLA film. Zeolite and ESO dispersed in the PLA matrix played a role in toughening and strengthening. The PLA/8 wt% zeolite/3 wt% ESO film had the highest longitudinal tensile strength at 77 MPa. The PLA/2 wt% zeolite/3 wt% ESO film had the highest longitudinal elongation at 13%. The physical properties depended heavily on the dispersion of zeolite and ESO in the matrix.

This work was designed to determine the mechanical properties and static cushioning performance of polyvinyl alcohol (PVA)/bagasse fibre foam composites with a multiple-factor experiment. Scanning electron microscopy (SEM) analysis and static cushioning tests were performed on the foamed composites and the results were compared with those of commonly used expanded polystyrene (EPS). The results were as follows: the materials had a mainly open cell structure, and bagasse fibre had good compatibility with PVA foam. With increasing PVA content, the mechanical properties of the system improved. The mechanical properties and static cushioning properties of the foam composite almost approached those of EPS. In addition, a small amount of sodium tetraborate obviously regulated the foaming ratio of foamed composites. With increasing sodium tetraborate content, the mechanical properties of foamed composites were enhanced. The yield strength and Young’s modulus of the material prepared by reducing the water content to 80.19 wt% were too high and not suitable for cushioned packaging of light and fragile products.