One of the attractive characteristics of high entropy alloys (HEAs) is the ability to tailor their composition to obtain specific microstructures and properties by adjusting the stoichiometry to obtain a body-centered cubic (BCC) or face-centered cubic (FCC) structure. Thus, in this work, the target composition of an alloy of the FeCrCoNi family has been modified by adjusting the Al/Cu ratio in order to obtain a BCC crystalline structure. However, processing conditions always play a key role in the final microstructure and, therefore, in this work, the microstructure evolution of FeCrCoNiAl_1.8Cu_0.5 HEA sintered by different powder metallurgy (PM) techniques has been investigated. The techniques used range from the conventional PM sintering route, that uses high heating rates and sintering times, going through a fast sintering technique such as spark plasma sintering (SPS) to the novel and promising ultrafast sintering technique electrical resistance sintering (ERS). Results show that the increase in the processing time favours the separation of phases and the segregation of elements, which is reflected in a substantial change in the hardness of the alloy. In conclusion, the ERS technique is presented as a very promising consolidation technique for HEA.

High production costs of Ti alloys usually hinders their use in industry sectors like the automotive and hence, low-cost titanium alloys could broaden titanium alloy usage. This work presents the study of three alloys— Ti-Fe, Ti-Fe-Al, and Ti-Fe-Cr—produced by powder metallurgy methods. The design of the compositions was aimed at reducing cost and enhance the oxidation and corrosion resistance while not decreasing the mechanical performance. The use of titanium hydride as raw material instead of Ti powder is highlighted as a key feature in the design and manufacturing procedure of the alloys. Introducing a dehydrogenation process during sintering favors the densification process while reducing the oxygen contamination and the production cost. There is a lack of studies focused on the implementation of affordable PM Ti alloys in high demanding environments. Therefore, a study of high temperature oxidation resistance and electrochemical behavior was performed.

The structure of FeCoNiCrAl1.8Cu0.5 high-entropy alloys (HEA) obtained by two different routes has been studied. The selection of the composition has followed the Hume–Rothery approach in terms of number of itinerant electrons (e/a) and average atomic radius to control the formation of specific phases. The alloys were obtained either from a mixture of elemental powders or from gas-atomised powders, being consolidated in both cases by uniaxial pressing and vacuum sintering at temperatures of 1200 °C and 1300 °C. The characterization performed in the sintered samples from both types of powder includes scanning electron microscopy, X-ray diffraction, differential thermal analysis, and density measurements. It was found that the powder production techniques give similar phases content. However, the sintering at 1300 °C destroys the achieved phase stability of the samples. The phases identified by all techniques and confirmed by Thermo-Calc calculations are the following: a major Co-Ni-Al-rich (P1) BCC phase, which stays stable after 1300 °C sintering and homogenising TT treatments; a complex Cr-Fe-rich (P2) B2 type phase, which transforms into a sigma phase after the 1300 °C sintering and homogenising TT treatments; and a very minor Al-Cu-rich (P3) FCC phase, which also transforms into Domain II and Domain III phases during the heating at 1300 °C and homogenising TT treatments.