The effect of anticancer drugs could be significantly enhanced if it is encapsulated in drug delivery vehicles such as liposomes, polymers, dendrimers and other materials. For some conventional cisplatin encapsulating methods, however, suffers from low loading efficiency. Therefore, in order to overcome this limitation, in our study, sonication was used in preparation of the nanocomplex of a species of aquated cisplatin and carboxylated PAMAM dendrimer G3.5 to evaluate loading capacity as well as plantinum release behavior using FT-IR, UV-Vis, NMR, ICP-AES, and TEM. The results show that 25.20 and 27.83 wt/wt% of cisplatin were loaded under stirring and sonication respectively, a remarkably improvement in loading efficiency compared to that of conventional method that used of cisplatin. In vitro study showed that this drug-nanocarrier complex also help reduce cisplatin's cytotoxicity but can still keep sufficient antiproliferative activity against lung cancer cell, NCI-H460, with IC50 at 0.985±0.01 μM.

Nanogel-based systems loaded with single anticancer drugs display miscellaneous effectiveness in tumor remission, gradually circumventing mutation and resistance in chemotherapy. Hence, the existence of dual-drug delivered nano-sized systems has been contemporaneous with drug development and preceded the conventional-dose chemotherapy. Among outstanding synergistic drug nanoplatforms, thermosensitive copolymer heparin-Pluronic F127 (Hep-F127) co-delivering cisplatin (CDDP) and curcumins (Cur) (Hep-F127/CDDP/Cur) has emerged as a notable candidate for temperature-responsive drug delivery. The procedure was based on the entrapment of curcumin into the hydrophobic core of bio-degradable co-polymer Hep-F127 while the hydrophilic drug CDDP subsequently conjugated to the backbone heparin to form the core-shell structure. The copolymer was characterized by Fourier transform infrared (FT-IR) spectrophotometry, Transmission Electron Microscopy (TEM), and Dynamic Light Scattering (DLS), to corroborate the successful synthesis and via HPLC along with AES-ICP to evaluate the high drug loading along with a controllable release from the nano-gels. A well-defined nano-shell with size in the 129.3 ± 3.8 nm size range could enhance higher the efficacy of the conjugated-CDDP to Hep-F127 than that of single doses. Moreover, the considerable amount of dual-drug released from thermosensitive nanogels between different conditions (pH = 7.4 and pH = 5.5) in comparison to CDDP from Hep-F127 partially indicated the significantly anti-proliferative ability of Hep-F127/CDDP/Cur to the MCF-7 cell line. Remarkably, drug testing in a xenograft model elucidates the intricate synergism of co-delivery in suppressing tumor growth, which remedies some of the problems affecting in cancer chemotherapy.

Nanosized multi-drug delivery systems provide synergistic effects between drugs and bioactive compounds, resulting in increased overall efficiency and restricted side effects compared to conventional single-drug chemotherapy. In this study, we develop an amphiphilic heparin-poloxamer P403 (HP403) nanogel that could effectively co-load curcuminoid (Cur) and cisplatin hydrate (CisOH) (HP403@CisOH@Cur) via two loading mechanisms. The HP403 nanogels and HP403@CisOH@Cur nanogels were closely analyzed with ¹H-NMR spectroscopy, FT-IR spectroscopy, TEM, and DLS, exhibiting high stability in spherical forms. In drug release profiles, accelerated behavior of Cur and CisOH at pH 5.5 compared with neutral pH was observed, suggesting effective delivery of the compounds in tumor sites. In vitro studies showed high antitumor activity of HP403@CisOH@Cur nanogels, while in vivo assays showed that the dual-drug platform prolonged the survival time of mice and prevented tail necrosis. In summary, HP403@CisOH@Cur offers an intriguing strategy to achieve the cisplatin and curcumin synergistic effect in a well-designed delivery platform that increases antitumor effectiveness and overcomes undesired consequences caused by cisplatin in breast cancer treatment.

Blue-emitting Ag⁽⁺⁾-, Cu⁽²⁺⁾-, and Mg⁽²⁺⁾-doped ZnSe nanoparticles (NPs) were successfully synthesized at 80 °C by the precipitation method by using mercaptopropionic acid (MPA) as a stabilizer. UV–visible and photoluminescence (PL) studies were applied to investigate their physicochemical properties. Their structural properties were confirmed by X-ray diffraction (XRD), Fourier transform infrared (FT-IR) and transmission electron microscopy (TEM). The size of the ZnSe: X-capped MPA showed a strong relationship with dopant metals. The diameters of the Mg-doped ZnSe and the Cu-doped ZnSe were 22–24 nm, while the Ag-doped ZnSe was halved, at about 13 nm. The photoluminescence was within a wavelength range of 400–550 nm. In addition, the PL intensities, as well as the photoluminescence quantum yields, were in the order of the decreasing ionic radii of the dopant metals (ZnSe:Ag < ZnSe:Mg < ZnSe:Cu). Furthermore, through the interaction with lysine, the PL intensity of the ZnSe:X was changed. Interestingly, the capacity of the ZnSe:Mg for lysine was significantly higher than that of other dopant metals. Moreover, the toxicity of the ZnSe:Mg was relatively insignificant toward the hMSCs (about 80% cell viability at 320 ppm), compared to the transition-metal dopant. Therefore, the ZnSe:Mg material could have great potential for bioapplications.