Ag@AgCl core–shell nanowires were synthesized by oxidation of Ag nanowires with moderate FeCl3, which exhibited excellent photocatalytic activity for As(III) oxidation under visible light. It was proved that the photocatalytic oxidation efficiency was significantly dependent on the mole ratio of Ag:AgCl. The oxidation rate of As(III) over Ag@AgCl core–shell nanowires first increased with the decrease of Ag0 percentage, up until the optimized synthesis mole ratio of Ag nanowires:FeCl3 was 2.32:2.20, with 0.023 mg L−1 min−1 As(III) oxidation rate; subsequently, the oxidation rate dropped with the further decrease of Ag0 percentage. Effects of the pH, ionic strength, and concentration of humic acid on Ag@AgCl photocatalytic ability were also studied. Trapping experiments using radical scavengers confirmed that h+ and ·O2 − acted as the main active species during the visible-light-driven photocatalytic process for As(III) oxidation. The recycling experiments validated that Ag@AgCl core–shell nanowires were a kind of efficient and stable photocatalyst for As(III) oxidation under visible-light irradiation.

A relatively low voltage can be favor of e^- transfer and peroxide generation from dominant 2e^--reduction of O₂ on carbon materials as cathode, with low energy loss. In this study the conversion of As(III) in simulated high arsenic groundwater at low voltage was compared in a mixed and a anode–cathode separated electrolytic system. With applied voltages (the potential difference between cathode and anode) from 0.1 V to 0.8 V, As(III) was found to be efficiently converted to As(V) in the mixed electrolytic cells and in separated anodic cells. The complete oxidation of As(III) to As(V) at 0.1–0.8 V was also achieved on graphite in divided cathodic cells which could be long-running. The As(III) conversion process in mixed electrolytic cells, anodic cells and cathodic cells all conformed to the pseudo first-order kinetics equation. The energy consumed by As(III) conversion was decreased as the applied voltage declined. Low voltage electrolysis is of great significance for saving energy consumption and improving the current efficiency and can be applied to in-situ electrochemical pre-oxidation for As(III) in high arsenic groundwater.