Premature drug release and poor controllability is a challenge in the practical application of tumor therapy, which may lead to poor chemotherapy efficacy and severe adverse effects. In this study, a reactive oxygen species (ROS)-cleavable nanoparticle system (MXene-TK-DOX@PDA) was designed for effective chemotherapy drug delivery and antibacterial applications. Doxorubicin (DOX) was conjugated to the surface of (3-aminopropyl)triethoxysilane (APTES)-functionalized MXene via an ROS-cleavable diacetoxyl thioketal (TK) linkage. Subsequently, the surfaces of the MXene nanosheets were coated with pH-responsive polydopamine (PDA) as a gatekeeper. PDA endowed the MXene-TK-DOX@PDA nanoparticles with superior biocompatibility and stability. The MXene-TK-DOX@PDA nanoparticles had an ultrathin planar structure and a small lateral size of approximately 180 nm. The as-synthesized nanoparticles demonstrated outstanding photothermal conversion efficiency, superior photothermal stability, and a remarkable extinction coefficient (23.3 L g⁻¹ cm⁻¹ at 808 nm). DOX exhibited both efficient ROS-responsive and pH-responsive release performance from MXene-TK-DOX@PDA nanoparticles due to the cleavage of the thioketal linker. In addition, MXene-TK-DOX@PDA nanoparticles displayed high antibacterial activity against both Gram-negative Escherichia coli (E. coli) and Gram-positive Bacillus subtilis (B. subtilis) within 5 h. Taken together, we hope that MXene-TK-DOX@PDA nanoparticles will enrich the drug delivery system and significantly expand their applications in the biomedical field

In this study, a novel MXene (Ti₃C₂T_x)-based nanocarrier was developed for drug delivery. MXene nanosheets were functionalized with 3, 3′-diselanediyldipropionic acid (DSeDPA), followed by grafting doxorubicin (DOX) as a model drug to the surface of functionalized MXene nanosheets (MXene-Se-DOX). The nanosheets were characterized using scanning electron microscopy, atomic force microscopy (AFM), transmission electron microscopy, energy-dispersive X-ray spectroscopy (EDX), nuclear magnetic resonance spectroscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and zeta potential techniques. The drug-loading capacity (17.95%) and encapsulation efficiency (41.66%) were determined using ultraviolet–visible spectroscopy. The lateral size and thickness of the MXene nanosheets measured using AFM were 200 nm and 1.5 nm, respectively. The drug release behavior of the MXene-Se-DOX nanosheets was evaluated under different medium conditions, and the nanosheets demonstrated outstanding dual (reactive oxygen species (ROS)- and pH-) responsive properties. Furthermore, the MXene-Se-DOX nanosheets exhibited excellent antibacterial activity against both Gram-negative E. coli and Gram-positive B. subtilis.

Despite their excellent properties, epoxy resins have the disadvantage of low toughness. With the aim to improve the toughness of epoxy resin, polyol and polyurethane are synthesized using bisphenol‐Z (BPZ). The synthesized material is dispersed in the epoxy resin and used as a toughening agent. Polyol (modified bisphenol‐Z [MBPZ]‐OH) is synthesized by a ring‐opening polymerization of propylene oxide and caprolactone, and polyurethane (MBPZ‐PU) is synthesized by a one‐shot method using MBPZ‐OH and hexamethylene diisocyanate (HMDI). The effect of MBPZ‐PU on the mechanical strength of the epoxy resin is analyzed by monitoring the flexural and impact characteristics. The addition of the synthesized MBPZ‐PU improves the tensile strength, flexural strength, flexibility, and impact strength of the cured epoxy composite. Field‐emission scanning electron microscopy measurements indicate that the fracture surface had a specific pattern. Thermal properties such as the curing temperature, glass transition temperature (T_g), and modulus are investigated through differential scanning calorimetry, dynamic mechanical analysis, and thermomechanical analysis. Based on the results, MBPZ‐PU is expected to be applied to a wider field for increasing the toughness of epoxy.

Highly monodispersed silica nanoparticles (SiNPs) were synthesised using a fluorinated surfactant, HOCH₂CH(CF₃)CO₂H, and its efficiency was compared with efficiencies of five other surfactants. The size of the SiNPs (∼50–200 nm) was controlled by controlling the surfactant amount. The short alkyl-chain fluoro surfactant was found to be more efficient at producing monodispersed SiNPs than its long alkyl-chain fluoro or non-fluorinated surfactant counterparts.