As lithium-ion battery (LIB) anode materials, porous carbons with high specific surface area are highly required because they can well accommodate huge volume expansion/contraction during cycling. In this work, hierarchically porous carbon (HPC) with high specific surface area (~1714.83 m² g⁻¹) is synthesized from biomass reed flowers. The material presents good cycling stability as an LIB anode, delivering an excellent reversible capacity of 581.2 mAh g⁻¹ after cycling for 100 cycles at a current density of 100 mA g⁻¹, and still remains a reversible capacity of 298.5 mAh g⁻¹ after cycling for 1000 cycles even at 1000 mA g⁻¹. The good electrochemical performance can be ascribed to the high specific surface area of the HPC network, which provides rich and fast paths for electron and ion transfer and provides large contact area and mutual interactions between the electrolyte and active materials. The work proposes a new route for the preparation of low cost carbon-based anodes and may promote the development of other porous carbon materials derived from various biomass carbon sources.

An exceptionally high-strength rare-earth-free Mg–8Al–3Bi (AB83) alloy was successfully fabricated via extrusion and caliber rolling. After three-pass caliber rolling, the homogenous microstructure of the as-extruded AB83 alloy was changed to a necklace-like bimodal structure consisting of ultra-fine dynamic recrystallized (DRXed) grains and microscale deformed grains. Additionally, both Mg₁₇Al₁₂ and Mg₃Bi₂ nanoprecipitates, undissolved microscale Mg₁₇Al₁₂, and Mg₃Bi₂ particles were dispersed in the matrix of caliber-rolled (CRed) AB83 alloy. The CRed AB83 sample demonstrated a slightly weakened basal texture, compared with that of the as-extruded sample. Consequently, CRed AB83 showed a tensile yield strength of 398 MPa, an ultimate tensile strength of 429 MPa, and an elongation of 11.8%. The superior mechanical properties of the caliber-rolled alloy were mainly originated from the combined effects of the necklace-like bimodal microstructure containing ultra-fine DRXed grains, the homogeneously distributed nanoprecipitates and microscale particles, as well as the slightly modified basal texture.