Due to the excellent properties of carbon fiber-reinforced polymers (CFRPs), such as high strength and strong corrosion resistance, the traditional water-jet-guided laser (WJGL) technology has problems with fiber pull-out and has a small cutting depth when processing CFRPs. Therefore, in this study, we used high-power water-jet-guided laser (HPWJGL) technology to perform groove processing experiments on CFRPs. The effects of four key process parameters, high laser power, pulse frequency, feed rate, and water-jet pressure, on the cutting depth were investigated by a single-factor experiment. The formation mechanism of groove cross-section morphology and the processing advantages of high-power water-jet-guided lasers were analyzed. On this basis, the mathematical prediction model of cutting depth was established by using the response surface method (RSM), and the optimal combination of process parameters was obtained. The mathematical prediction model was verified by experiments, and the error was only 1.84%, indicating that the model had a high reference value. This study provides a reference for the precision machining of HPWJGL technology.

In this investigation, spherical Al₂O₃ magnetic abrasive particles (MAPs) were used to polish the inner surface of ultra-fine long cobalt–chromium alloy cardiovascular stent tubes. The magnetic abrasives were prepared by combining plasma molten metal powder and hard abrasives, and the magnetic abrasives prepared by this new method are characterized by high sphericity, narrow particle size distribution range, long life, and good economic value. Firstly, the spherical Al₂O₃ magnetic abrasives were prepared by the new method; secondly, the polishing machine for the inner surface of the ultra-fine long cardiovascular stent tubes was developed; finally, the influence laws of spindle speed, magnetic pole speed, MAP filling quantities, the magnetic pole gap on the surface roughness (Ra), and the removal thickness (RT) of tubes were investigated. The results showed that the prepared Al₂O₃ magnetic abrasives were spherical in shape, and their superficial layer was tightly bound with Al₂O₃ hard abrasives with sharp cutting; the use of spherical Al₂O₃ magnetic abrasives could achieve the polishing of the inner surface of ultra-fine cobalt–chromium alloy cardiovascular bracket tubes, and after processing, the inner surface roughness (Ra) of the tubes decreased from 0.337 µm to 0.09 µm and had an RT of 5.106 µm.

There are high cutting temperatures, large tool wear, and poor tool life in conventional machining, owing to the superior strength and low thermal conductivity of titanium alloy. In this work, ultrasonic atomization assisted turning (UAAT) of Ti6Al4V was performed with a mixed water-soluble oil-based cutting fluid, dispersed into tiny droplets by the high frequency vibration of a piezoelectric crystal. Different cutting speeds and two machining environments, dry and ultrasonic atomization assisted machining, were considered in the investigation of tool life, tool wear morphology, surface roughness, and chip morphology. In comparison with dry machining, UAAT shows lower tool wear and longer tool life due to the advantages of cooling and lubrication. Furthermore, better surface roughness, smoother chip edges, and shorter tool-chip contact length were obtained with UAAT.