The methods of synthesis of silver (Ag) nanoparticles by the cyanobacteria Spirulina platensis and Nostoc linckia were studied. A complex of biochemical, spectral, and analytical methods was used to characterize biomass and to assess changes in the main components of biomass (proteins, lipids, carbohydrates, and phycobilin) during nanoparticle formation. The size and shape of Ag nanoparticles in the biomass of both types of cyanobacteria were determined. Neutron activation analysis was used to study the accumulation dynamics of the Ag quantity. The analytical results suggest that the major reduction of Ag concentration in solutions and the increase in biomass occur within the first 24 h of experiments. While in this time interval minor changes in the N. linckia and S. platensis biomass took place, a significant reduction of the levels of proteins, carbohydrates, and phycobiliproteins in both cultures and of lipids in S. platensis was observed after 48 h. At the same time, the antiradical activity of the biomass decreased. The obtained results show the necessity of determining the optimal conditions of the interaction between the biomass and the solution containing Ag ions that would allow nanoparticle formation without biomass degradation at the time of Ag nanoparticle formation by the studied cyanobacteria.

The process of selenium uptake by biomass of the cyanobacterium Arthrospira (Spirulina) platensis was investigated by neutron activation analysis at different selenium concentrations in solution and at different contact times. Experimental data showed good fit with the Freundlich adsorption isotherm model, with a regression coefficient value of 0.99. In terms of absorption dependence on time, the maximal selenium content was adsorbed in the first 5 min of interaction without significant further changes. It was also found that A. platensis biomass forms spherical selenium nanoparticles. Biochemical analysis was used to assess the changes in the main components of spirulina biomass (proteins, lipids, carbohydrates, and phycobilin) during nanoparticle formation.

Anthropogenic activity is the main factor contributing to soil pollution with various toxic metals, including Cr(VI), which dictates the need for decontamination. Often, the traditionally used remediation methods (soil removal, stabilization/solidification, physicochemical extraction, and soil washing) are not sufficiently efficient. Among gentle soil remediation, options can be considered. The aim of this study is to assess the ability of Nostoc linckia to remediate soils contaminated with Cr(VI) in association with other metals. Metal uptake by biomass was assessed using neutron activation analysis, while the components of Nostoc biomass were determined using specific methods. The capacity to accumulate chromium from the contaminated environment (Cr in association with Fe, Ni, Cu, and Zn) by the Nostoc linckia is kept at a high level for three generations of cyanobacterium, and the capacity to accumulate Fe, Ni, Cu, and Zn is growing over the cultivation cycles. The process of accumulation of heavy metals is associated with significant changes in the biochemical composition of Nostoc biomass. Due to the high bioaccumulation capacity and the specific growth mode with the formation of crusts on the soil surface, the edaphic cyanobacteria Nostoc linckia is an important candidate for the bioremediation of soil contaminated with chromium in association with other metals.

Silver and gold nanoparticles are promising tools for medical and industrial applications; therefore, their ecotoxicity should be carefully examined. There are many publications that discuss their effects at high concentrations on various organisms, while the effects of low doses have not been sufficiently investigated. In this paper, the effects of low concentrations of silver (12 nm) and gold (4.7 nm) nanoparticles coated with polyethylene glycol on Spirulina platensis biomass growth, biochemical composition, and antioxidant activity were investigated. The spirulina cultivation medium was supplemented with nanoparticles in the concentration range of 0.025–0.5 µM. The given concentrations stimulated spirulina biomass, but the content of proteins, carbohydrates, and auxiliary pigments was insignificantly affected by the presence of nanoparticles in the cultivation medium. Gold nanoparticles at a concentration of 0.5 µM produced a pronounced effect on the lipid content. Transmission electron microscope images demonstrated that the nanoparticles penetrate inside the cells and cause ultrastructural changes. The nanoparticles were characterized using several well-known techniques. The results confirmed a negative effect of low concentrations of metal nanoparticles on spirulina. This effect could be indiscernible when studying the biomass viability, but determination of the ultrastructure of the cell and the biochemical composition of the biomass could reveal it.