Nylon (PA) netting is widely used in purse seines and other fishing gears due to its high strength and good sinking performance. However, hydrodynamic properties of nylon netting of different characteristics are poorly understood. This study investigated hydrodynamic characteristics of nylon netting of different knot types and solidity ratios under different attack angles and flow velocities. It was found that the hydrodynamic coefficient of netting panels was related to Reynolds number, solidity ratio, attack angle, knot type and twine construction. The solidity ratio was found to positively correlate with drag coefficient when the netting was normal to the flow (C_D90), but not the case when the netting was parallel to the flow (C_D0). For netting panels inclined to the flow, the inclined drag coefficient had a negative relationship with the solidity ratio for attack angles between 0° and 50°, but a positive relationship for attack angles between 50° and 90°. The lift coefficient increased with the attack angle, reaching the culminating point at an attack angle of 50°, before subsequent decline. We found that the drag generated by knot accounted for 15–25% of total drag, and the knotted netting with higher solidity ratio exhibited a greater C_D0, but it was not the case for the knotless netting. Compared to knotless polyethylene (PE) netting, the drag coefficients of knotless PA netting were dominant at higher Reynolds number (Re>2200).

It is essential to conduct hydrodynamic experiments for fishing gear at small attack angles along the flow direction to better understand the hydrodynamic characteristics of netting and application of gear. The hydrodynamic characteristics of netting panels made of different materials at small attack angles were investigated by a self-designed setup; this is essential for the effective use of netting on different types of gears. As confirmed by experiments, the measured drag of designed frame without netting accounted for less than 20% of the total setup drag including experimental netting and remained in a steady state under various current speeds and small attack angles, indicating that the self-designed frame setup is suitable for such trials. The drag coefficient was determined by varying the attack angle, solidity ratio, Reynolds number, knot types, weave pattern, and twine materials at small attack angles. The results indicate that the drag coefficient increased as the attack angle increased, but decreased as the solidity ratio and Reynolds number increased. The drag generated by knot accounted for 21% of the total drag of nylon (PA) netting. For braided knotless netting, the drag coefficient of PA netting was about 8.4% lower than that of polythene netting (PE) and 7% lower than that of polyester netting (PES). Compared with twined netting, the braided netting exhibited a higher resistance to flow, corresponding to higher values of drag coefficient.