The polymer laser sintering (PLS) process is one of the most promising additive manufacturing (AM) technologies for polymeric materials. However, the technique has challenges because the physical, mechanical, and chemical properties of the polymeric powder deteriorate due to the high temperatures prevailing in the build chamber during manufacture. These high temperatures cause agglomeration of powder, which leads to a decrease in the flowability of powder. There is also a related drop in the coalescence of the powder granules during PLS, which results in porosity that undermines the mechanical integrity of printed parts. Moreover, the viscosity of the melt increases due to cross-linking of molecular chains. This, in turn, increases the tensile strength of the printed components at the expense of the percentage elongation at break. Thus, high prolonged processing temperatures decrease the reusability of polymeric materials used in PLS. In this paper, a review of the studies conducted to investigate ways of reducing the effects of high temperature on polymeric powders is presented.

Additive manufacturing (AM), is one of the key components of the 4th industrial revolution. Polymer laser sintering (PLS) is a subset of AM that is commonly used to process polymers, and which achieves good surface finish, good mechanical properties of finished products and for which there is no need for support structures. However, the requirements for polymeric powder for PLS are strident. Moreover, PLS subjects polymeric feed powders to high temperatures that lead to degradation of their thermal, rheological, and physical properties and is thus an impediment to their recyclability. Therefore, it is imperative to investigate the degree of polymer degradation or aging before re-using the material. This paper reviews the common techniques that are employed to characterize the suitability of polymeric powders for use and re-use in the PLS process. These include, but are not limited to, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), laser diffraction analysis, gas pycnometry, scanning electron microscopy (SEM), and melt flow index (MFI) testing.

In the present study, recyclability of Laser PP CP 75 polypropylene powder from Diamond Plastics GmbH was determined by characterizing and comparing the used powder after each cycle with material from previous cycles and with fresh powder. The melt flow index of Laser PP CP 75 was affected by recycling since it was observed to change by 30.62% after the 8th 100% re-use cycle, a lower value than PA 12 of 66.04%, for the 6th re-use cycle. Parts printed with virgin Laser PP CP 75 had an average dimensional error of 3.02% (virgin material) and 4.06% after the 4th 100% re-use cycle, which raises concerns about the commercial viability of the material. After the 4th re-use cycle, the printed parts had distorted edges and failed to print after the 9th print cycle. Lastly, tensile testing revealed a skewed bell-shaped curve of strength versus the number of recycles with the highest ultimate tensile strength occurring for the second 100% re-use cycle (7.4 MPa). The curves for elastic modulus and percentage elongation were inverted with minimum points for the 2nd 100% re-use cycle. Overall, the experimental work confirmed that the properties of polypropylene powder were affected by recycling in polymer laser sintering, but the powder exhibited superior characteristics upon recycling to those of the predominantly used PA 12 powder.

The uptake of laser powder bed fusion for polymers has remained limited mainly because the interaction between material properties and process parameters is not well understood. The constraints of experimentally determining the optimal process parameters for new polymers in laser powder bed fusion include high expense, time-consumption, errors, and considerable effort. Hence, the need for using analytical and numerical models as alternatives. This paper starts with a summary on laser powder bed fusion of polymers, reviews the aspects of the process requiring the use of analytical and numerical tools, limitations, and possible improvements of the existing studies on the analytical models, and finally briefly explores approaches for numerical modelling of laser powder bed fusion of polymers. Some of the key aspects of the process that have been identified as being amenable to modelling include powder spreading and deposition of the layers, interaction between the laser beam and powder particles, melting and fusion of the particles, powder bed surface temperature, heat transfer through the powder, cooling phase, and the properties of printed parts. It is suggested in the study that the existing analytical and/or numerical models can be improved by increasing relevant variables (process parameters and material characteristics) used in them.