Cellulose nanomaterials (CNs) are renewable, bio-derived materials that can address not only technological challenges but also social impacts. This ability results from their unique properties, for example, high mechanical strength, high degree of crystallinity, biodegradable, tunable shape, size, and functional surface chemistry. This minireview provides chemical and physical features of cellulose nanomaterials and recent developments as an adsorbent and an antimicrobial material generated from bio-renewable sources.

In this report, we focus our effort to extract cellulose nanomaterials (CNs) from an agricultural cellulosic waste, Dragon Fruit foliage (DFF). DFF was first pretreated by several mechanical treatments and then bleached by chemical treatment to obtain bleached DFF. CNs were then produced from the hydrolysis of the bleached DFF catalyzed by sulfuric acid. We obtained CNs with a small diameter (50 to 130 nm) and length (100 to 500 nm) and a height of 3 to 10 nm. The CNs have a high crystallinity (crystallinity index 84.8%), high −COOH content (0.74 mmol·g⁻¹), good thermal stability and a good Cu (II) adsorption capacity with an adsorption maximum of ~103 mg·g⁻¹. These findings demonstrated the great potential of converting many agricultural cellulosic wastes into valuable cellulose nanomaterials.

The control of the interface and the adhesion process are key issues for the development of new application based on electrochromic materials. In this work the functionalization of an electrode’s surface through electroreduction of diazonium generated in situ from 4-(2,5-di-thiophen-2-yl-pyrrol-1-yl)-phenylamine (SNS-An) has been proposed. The synthesis of the aniline derivative SNS-An was performed and the electrografting was investigated by cyclic voltammetry on various electrodes. Then the organic thin film was fully characterized by several techniques and XPS analysis confirms the presence of an organic film based on the chemical composition of the starting monomer and allows an estimation of its thickness confirmed by AFM scratching measurements. Depending on the number of electrodeposition cycles, the thickness varies from 2 nm to 10 nm, which corresponds to a few grafted oligomers. In addition, the grafted film showed a good electrochemical stability depending on the scan rates up to 400 V/s and the electrochemical response of the modified electrode towards several redox probes showed that the attached layer acts as a conductive switch. Therefore, the electrode behaves as a barrier to electron transfer when the standard redox potential of the probe is below the layer switching potential, whereas the layer can be considered as transparent towards the electron transfer for redox probes with a redox potential above it.