This study aims to provide an overview of the growing need for renewable energy conversion and aligns with the broader context of environmentally friendly energy, specifically through producing syngas from biomass. Unlike natural gas, which is mainly composed of methane, syngas contains a mixture of combustible CO, H₂, and C_nH_m. Therefore, optimizing its production requires a thorough examination of various operational parameters such as the gasifying agent, the equivalence ratio, the biofuel type, and the state, particularly in densified forms like pellets or briquettes. As new biomass sources are continually discovered and tested, operational parameters are also constantly evaluated, and new techniques are continuously developed. Indeed, these techniques include different gasifier types and the use or non-use of catalysts during biofuel conversion. The present study focuses on these critical aspects to examine their effect on the efficiency of syngas production. It is worth mentioning that syngas is the primary gaseous product from gasification. Moreover, it is essential to note that the pyrolysis process (prior to gasification) can produce, in addition to tar and char, a mixture of gases. The common feature among these gases is their versatility in energy generation, heat production, and chemical synthesis. The analysis encompasses the resulting gas features, including the yield and composition, mainly through the hydrogen-to-carbon monoxide ratio and the carbon monoxide-to-carbon dioxide ratio, as well as the lower heating value and considerations of the tar yield.

This paper aims at investigating the production of high quality briquettes from olive mill solid waste (OMSW) mixed with corn starch as a binder for energy production. For this purpose, different mass percentages of OMSW and binder were considered; 100%-0%, 90%-10%, 85%-15%, and 70%-30%, respectively. The briquetting process of the raw mixtures was carried out based on high pressures. Physico-chemical and mechanical characterizations were performed in order to select the best conditions for the briquettes production. It was observed that during the densification process, the optimal applied pressure increases notably the unit density, the bulk density, and the compressive strength. Mechanical characterization shows that the prepared sample with 15% of corn starch shows the best mechanical properties. Moreover, the corn starch binder affects quietly the high heating value (HHV) which increases from 16.36 MJ/Kg for the 100%-0% sample to 16.92 MJ/Kg for the 85%-15% sample. In addition, the kinetic study shows that the binder agent does not affect negatively the thermal degradation of the briquettes. Finally, the briquettes characterization shows that the studied samples with particles size less than 100 μm and blended with 15% of corn starch binder are promising biofuels either for household or industrial plants use.