The ICIE16-bioactive glass (BG) (48.0 SiO₂, 6.6 Na₂O, 32.9 CaO, 2.5 P₂O₅, 10.0 K₂O (wt %)) has been developed as an alternative to 45S5-BG, the original BG composition (45.0 SiO₂, 24.5 Na₂O, 24.5 CaO, 6.0 P₂O₅ (wt %)), with the intention of broadening the BG sintering window while maintaining bioactivity. Because there is a lack of reports on ICIE16-BG biological properties, the influence of ICIE16-BG on viability, proliferation, and osteogenic differentiation of human mesenchymal stromal cells (MSCs) was evaluated in direct comparison to 45S5-BG in this study. The BGs underwent heat treatment similar to that which is required in order to fabricate scaffolds by sintering, which resulted in crystallization of 45S5-BG (45S5-CBG) while ICIE16 remained amorphous. Granules based on both BGs were biocompatible, but ICIE16-BG was less harmful to cell viability, most likely due to a more pronounced pH alkalization in the 45S5-CBG group. ICIE16-BG outperformed 45S5-CBG in terms of osteogenic differentiation at the cellular level, as determined by the increased activity of alkaline phosphatase. However, granules from both BGs were comparable regarding the stimulation of expression levels of genes encoding for osseous extracellular matrix (ECM) proteins. The addition of therapeutically active ions to ICIE16-BG might further improve its ability to stimulate ECM production and should be investigated in upcoming studies.

Magnesium (Mg²⁺) is known to play a crucial role in mineral and matrix metabolism of bone tissue and is thus increasingly considered in the field of bone tissue engineering. Bioactive glasses (BGs) offer the promising possibility of the incorporation and local delivery of therapeutically active ions as Mg²⁺. In this study, two Mg²⁺-doped derivatives of the ICIE16-BG composition (49.46 SiO₂, 36.27 CaO, 6.6 Na₂O, 1.07 P₂O₅, 6.6 K₂O (mol%)), namely 6Mg-BG (49.46 SiO₂, 30.27 CaO, 6.6 Na₂O, 1.07 P₂O₅, 6.6 K₂O, 6.0 MgO (mol%) and 3Mg-BG (49.46 SiO₂, 33.27 CaO, 6.6 Na₂O, 1.07 P₂O₅, 6.6 K₂O, 3.0 MgO (mol%)) were examined. Their influence on viability, proliferation and osteogenic differentiation of human mesenchymal stromal cells (MSCs) was explored in comparison to the original ICIE16-BG. All BGs showed good biocompatibility. The Mg²⁺-doped BGs had a positive influence on MSC viability alongside with inhibiting effects on MSC proliferation. A strong induction of osteogenic differentiation markers was observed, with the Mg²⁺-doped BGs significantly outperforming the ICIE16-BG regarding the expression of genes encoding for protein members of the osseous extracellular matrix (ECM) at certain observation time points. However, an overall Mg²⁺-induced enhancement of the expression of genes encoding for ECM proteins could not be observed, possibly due to a too moderate Mg²⁺ release. By adaption of the Mg²⁺ release from BGs, an even stronger impact on the expression of genes encoding for ECM proteins might be achieved. Furthermore, other BG-types such as mesoporous BGs might provide a higher local presence of the therapeutically active ions and should therefore be considered for upcoming studies.

The present study reports the dissolution studies of a family of boron-doped bioactive glasses based on the composition ICIE16. Simulated body fluid (SBF), Tris-buffered solution and lactic acid were used as dissolution media for studies under static and dynamic conditions. The leaching of ions from the glasses under the evaluated conditions and media was compared and the bioactive behaviour of the glasses was evaluated. Influence of the incorporation of boron in the thermal properties of the glass was also analysed. Glasses exhibited faster bioactivity under dynamic dissolution configuration compared to static conditions. Moreover, the glass dissolution rate was faster in acidic conditions than in SBF or Tris solutions. It was found that at increasing boron content the dissolution of the glass is faster.

Due to their high bioreactivity, the in-vitro analysis of bioactive glasses (BGs) can be challenging when it comes to maintaining a physiological pH. To improve BG biocompatibility, a heterogenic spectrum of preconditioning approaches, such as “passivation” of the BGs by incubation in cell culture medium, are used but have never been directly compared. In this study, the effect of passivation periods of up to 72 h on pH alkalization and viability of human bone marrow-derived mesenchymal stromal cells was evaluated to determine a time-efficient passivation protocol using granules based on the 45S5-BG composition (in wt%: 45.0 SiO₂, 24.5 Na₂O, 24.5 CaO, 6.0 P₂O₅) in different concentrations. pH alkalization was most reduced after passivation of 24 h. Cell viability continuously improved with increasing passivation time being significantly higher after passivation of at least 24 h compared to non-passivated 45S5-BG and the necessary passivation time increased with increasing BG concentrations. In this setting, a passivation period of 24 h presented as an effective approach to provide a biocompatible cell culture setting. In conclusion, before introduction of BGs in cell culture, different passivation periods should be evaluated in order to meet the respective experimental settings, e.g., by following the experimental protocols used in this study.