The novel poly(vinyl alcohol) (PVA)-based membranes were prepared using the two-step crosslinking approach: the chemical crosslinking of PVA using sulfosuccinic acid (SSA) (0–50 wt.%) and the thermal treatment (120–160 °C). The membrane composition and crosslinking temperature were optimized in terms of the mechanical and transport properties. The FTIR-ATR analysis revealed that the increase of the SSA concentration and crosslinking temperature resulted in the rise of the ester bond bands intensity due to the esterification reaction between PVA and SSA. As a consequence, the PVA-based membrane with 50 wt % SSA and crosslinked at 140 °C showed the reduced Young’s modulus (from 1266.2 MPa to 1.4 MPa) and elongation at break (from 316% to 66%) in comparison with the pure PVA membrane. The studied swelling behavior of the obtained membranes revealed significantly higher water sorption than that in methanol and propal-2-ol whatever the crosslinking temperature. The performed studies provide a new way of tailoring the membrane physicochemical properties, in particular, the surface hydrophilicity. In addition, the obtained results are crucial for the design and elaboration of the polymer membranes for the pervaporative separation of the liquid-liquid mixtures, in particular, for the alcohol dehydration.

Today, the use of polymer electrolyte membranes (PEMs) possessing ionic liquids (ILs) in middle and high temperature polymer electrolyte membrane fuel cells (MT-PEMFCs and HT-PEMFCs) have been increased. ILs are the organic salts, and they are typically liquid at the temperature lower than 100 °C with high conductivity and thermal stability. The membranes containing ILs can conduct protons through the PEMs at elevated temperatures (more than 80 °C), unlike the Nafion-based membranes. A wide range of ILs have been identified, including chiral ILs, bio-ILs, basic ILs, energetic ILs, metallic ILs, and neutral ILs, that, from among them, functionalized ionic liquids (FILs) include a lot of ion exchange groups in their structure that improve and accelerate proton conduction through the polymeric membrane. In spite of positive features of using ILs, the leaching of ILs from the membranes during the operation of fuel cell is the main downside of these organic salts, which leads to reducing the performance of the membranes; however, there are some ways to diminish leaching from the membranes. The aim of this review is to provide an overview of these issues by evaluating key studies that have been undertaken in the last years in order to present objective and comprehensive updated information that presents the progress that has been made in this field. Significant information regarding the utilization of ILs in MT-PEMFCs and HT-PEMFCs, ILs structure, properties, and synthesis is given. Moreover, leaching of ILs as a challenging demerit and the possible methods to tackle this problem are approached in this paper. The present review will be of interest to chemists, electrochemists, environmentalists, and any other researchers working on sustainable energy production field.

The surface functionalization of polyimide (Matrimid^® 5218) films was carried out by cold plasma treatment with CF₄, N₂ and O₂ gases using a radio frequency discharge and the optimum plasma conditions were evaluated by water contact angle measurements. The surface hydrophobicity of polyimide films was obtained after CF₄ plasma treatment, while O₂ and N₂ plasma treatments contributed to the hydrophilic surface functionalization. X-ray photoelectron spectroscopy (XPS) results revealed the presence of CF_x, amino or oxygen-containing groups attached to the polyimide film surface depending on the treatment gas. A strong influence of the used plasma gas on the film roughness was determined by atomic force microscopy (AFM) measurements. The influence of the surface modification on CO₂, N₂ and O₂ gas permeation through the plasma treated films was evaluated. The permeation behaviour was characterized in terms of transport parameters, namely, coefficients of permeability, diffusion and solubility. The permeability coefficient of all plasma treated polyimide films for the studied gases (CO₂, N₂ and O₂) was found to decrease following the order of increasing the kinetic molecular diameter of the penetrant gas. Besides, the selectivity coefficient was found to be significantly increased after the plasma treatments – α CO₂/N₂ was increased up to 36% and 98% for O₂ and N₂ plasma treated Matrimid^® 5218 films, respectively. The relationship between the gas permeation behaviour and the surface modification of polymer film by cold plasma was discussed.

Pervaporation is a membrane-separation technique which uses polymeric and/or ceramic membranes. In the case of pervaporation processes applied to dehydration, the membrane should transport water molecules preferentially. Reactive ionic liquid (RIL) (3-(1,3-diethoxy-1,3-dioxopropan-2-yl)-1-methyl-1H-imidazol-3-ium) was used to prepare novel dense cellulose acetate propionate (CAP) based membranes, applying the phase-inversion method. The designed polymer-ionic liquid system contained ionic liquid partially linked to the polymeric structure via the transesterification reaction. The various physicochemical, mechanical, equilibrium and transport properties of CAP-RIL membranes were determined and compared with the properties of CAP membranes modified with plasticizers, i.e., tributyl citrate (TBC) and acetyl tributyl citrate (ATBC). Thermogravimetric analysis (TGA) testified that CAP-RIL membranes as well as CAP membranes modified with TBC and ATBC are thermally stable up to at least 120 °C. Tensile tests of the membranes revealed improved mechanical properties reflected by reduced brittleness and increased elongation at break achieved for CAP-RIL membranes in contrast to pristine CAP membranes. RIL plasticizes the CAP matrix, and CAP-RIL membranes possess preferable mechanical properties in comparison to membranes with other plasticizers investigated. The incorporation of RIL into CAP membranes tuned the surface properties of the membranes, enhancing their hydrophilic character. Moreover, the addition of RIL into CAP resulted in an excellent improvement of the separation factor, in comparison to pristine CAP membranes, in pervaporation dehydration of propan-2-ol. The separation factor β increased from ca. 10 for pristine CAP membrane to ca. 380 for CAP-16.7-RIL membranes contacting an azeotropic composition of water-propan-2-ol mixture (i.e., 12 wt % water).

Four water insoluble room-temperature protic ionic liquids (PILs) based on the N-alkylimidazolium cation with the alkyl chain length from 1 to 4 and bis(trifluoromethylsulfonyl)imide anion were synthesized and their chemical structure was confirmed by the ¹H NMR and ¹⁹F NMR analysis. PILs were revealed to be thermally stable up to 360 and 400 °C. At the same time, the proton conductivity of PILs was found to be dependent mostly on the temperature and, to a less extent, on the type of the cation, i.e., the increase of the conductivity from ~3 × 10⁻⁴ S/cm at 25 °C to 2 × 10⁻² S/cm at 150 °C was observed. The water vapour sorption capacity of PILs was evaluated as a function of relative humidity and the influence of the alkyl chain length on the phase behaviour in the PIL-water system was discussed. The composite polyimide/PILs membranes were prepared by the PIL immobilization in the porous polymer (Matrimid^® 5218) film. The composite membranes showed a high level of proton conductivity (~10⁻³ S/cm) at elevated temperatures (up to 160 °C). The obtained results reveal that the elaborated composite polyimide/PIL membranes are promising candidates for the application as proton exchange membrane at middle and high temperatures.

Different hydrophobic plasma treatments (CF₄, CF₄/H₂, CF₄/C₂H₂, tetramethyl silane (TMS)) were applied to the poly(lactic acid) (PLA) film in order to improve its water and oxygen barrier properties. The plasma parameters, such as power, gas flow and treatment time, were optimized according to the water contact angle measurements. X-ray photoelectron spectroscopy measurements revealed the presence of either fluorine (CF, CF₂, CF₃) or silicon (SiO_xC_y) functional groups on the film surface after the fluorinated or TMS plasma treatments, respectively. The thermal properties of the treated PLA films were studied by means of the differential scanning calorimetry (DSC) measurements and were found not to be influenced by the plasma treatment. The water permeability measurements showed an improvement of the PLA barrier properties as a result of all plasma treatments used and, particularly, after CF₄/C₂H₂ plasma. The water vapour sorption measurements confirmed well the improvement of the water barrier properties by the reduction of the water solubility. No impact of the plasma treatment on the oxygen barrier properties of the PLA film was observed, even at high relative humidity (up to 90%).