Biolubricant from modified sesame oil (Sesamumindicum L.) was produced. The lubricant base consists of a mixture in a volume ratio of 74 parts of epoxidized sesame and 26 parts of transesterified sesame oil. This mixture was characterized by FT-IR, thermo-oxidative stability was determined and heating and cooling curves were performed, where a crystallization and solidification temperature of -8 °C was obtained. To improve the lubricating capacity of the oil blend concentrations of 0.05, 0.10, 0.15 and 0.20% of copper nanoparticles (NPsCu) and alumina nanoparticles (NPsAl2O3) were added, which had been subjected to tribological tests for the wear scar measurement and characterized by scanning electron microscopy (SEM). The addition of NPsCu and NPsAl2O3 improved the lubricating power of oil base-stock. The NPsCu percentage in modified sesame oil that showed the best lubricating performance was in the interval between 0.15-0.2; as for the oil with NPs2O3 better result was obtained with 0,05% of NPs.

Introduction: In recent years the research and development of biolubricants from vegetable oils has increased to minimize the impact on the environment of petroleum derivatives. Objective: In this work, there was realized a comparative study of the thermal properties of the oil of Sesame with those of two mineral oils, of medium and high viscosity (360 and 255), which were free of additives. Method: The characterization of the three oils was performed using the technique of infrared spectroscopy (FT-IR) and physical properties such as kinematic viscosity, density, thermal and oxidative properties were determined by the analysis of Differential Calorimetry Scanning (DSC). Results: The sesame oil had a pour point of – 14.67 ° C, lower temperature than for mineral oils of 255 and 360, (– 4.29 ° C and – 6.89 ° C, respectively). The high content of unsaturated fatty acids (84.86%) could be responsible for this behavior. The oils were stable to temperatures near to 250 °C and with nitrogen atmosphere. Mineral oils were more stable to oxidation because of their high content of fatty acids with saturated hydrocarbon chains which it had no oxidizable sites. Conclusions: Nevertheless, the low stability of sesame oil is due to the high content of unsaturated fatty acids, the use of antioxidant, additive or a chemical modification of the unsaturated chains, this property might be improved to use the oil as a lubricant. Introducción: En los últimos años, la investigación y el desarrollo de biolubricantes a partir de aceites vegetales ha aumentado para minimizar el impacto en el medio ambiente de los derivados del petróleo. Objetivo: En este trabajo, se realizó un estudio comparativo de las propiedades térmicas del aceite de sésamo con las de dos aceites minerales de viscosidad media y alta (360 y 255) libres de aditivos. Método: La caracterización de los tres aceites se realizó mediante la técnica de espectroscopia infrarroja (FT-IR) y propiedades físicas como viscosidad cinemática, densidad, propiedades térmicas y oxidativas se determinaron mediante el análisis del escaneo de calorimetría diferencial (ECD). Resultados: El aceite de sésamo tenía un punto de fluidez de - 14.67 ° C, temperatura más baja que para los aceites minerales 255 y 360, (- 4.29 ° C y - 6.89 ° C, respectivamente). El alto contenido de ácidos grasos insaturados (84.86%) podría ser responsable de este comportamiento. Los aceites fueron estables en temperaturas cercanas a 250 ° C y con atmósfera de nitrógeno. Los aceites minerales son más estables a la oxidación debido a su alto contenido de ácidos grasos con cadenas de hidrocarburos saturadas sin sitios oxidables. Conclusiones: Sin embargo, la baja estabilidad del aceite de sésamo se debe al alto contenido de ácidos grasos insaturados, el uso de antioxidantes, aditivos o una modificación química de las cadenas insaturadas, esta propiedad podría ser mejorada para usar el aceite como lubricante.

En esta investigación se evaluó el poder lubricante del aceite de almendras dulces (Prunus amygdalus var. dulcis) mediante ensayos de desgaste preventivo (AW) y presión extrema (EP) en un tribómetro cuatro bolas. Los resultados obtenidos, se compararon con el comportamiento de dos aceites minerales de diferente viscosidad, blanco técnico y plastificante delta 360, sin aditivos. Se determinó que el aceite de almendras dulces posee mayor poder lubricante con respecto a los aceites minerales. Las esferas lubricadas con aceite de almendras presentaron menor diámetro promedio de la huella de desgaste y menor coeficiente de fricción. Además, el aceite de almendras dulces presentó mejor desempeño en condiciones de extrema presión, mostrando un punto de soldadura mayor que los aceites minerales. Finalmente, mediante el análisis por espectroscopia FT-IR, se determinó que en las condiciones en las que se realizaron los ensayos el aceite de almendras no se oxida.

En el presente artículo se evalúan las propiedades mecánicas de los materiales compuestos basados en cenizas volantes de carbón de la central termoeléctrica de Termozipa combinadas con los película extensible (Stretch film), polietilenos de baja densidad lineal de pos-consumo y polímero termoplástico parcialmente cristalino pos- industrial. Se obtuvieron mezclas variando el contenido de cenizas volantes de 0 a 50 % en peso en cada uno de los tres materiales poliméricos, dentro de una máquina mezcladora tipo Brabender. Las propiedades mecánicas evaluadas fueron: resistencia a la tracción, dureza Shore D, y absorción de energía. Los resultados obtenidos indican que en todos los casos a medida que se agrega ceniza volante las propiedades mecánicas aumentan.