Biomaterials can be endowed with biologically instructive properties by changing basic parameters such as elasticity and surface texture. However, translation from in vitro proof of concept to clinical application is largely missing. Porous calcium phosphate ceramics are used to treat small bone defects but in general do not induce stem cell differentiation, which is essential for regenerating large bone defects. Here, we prepared calcium phosphate ceramics with varying physicochemical and structural characteristics. Microporosity correlated to their propensity to stimulate osteogenic differentiation of stem cells in vitro and bone induction in vivo. Implantation in a large bone defect in sheep unequivocally demonstrated that osteoinductive ceramics are equally efficient in bone repair as autologous bone grafts. Our results provide proof of concept for the clinical application of “smart” biomaterials.

Antimicrobial resistance is a multifaceted crisis, imposing a serious threat to global health. The traditional antibiotic pipeline has been exhausted, prompting research into alternate antimicrobial strategies. Inspired by nature, antimicrobial peptides are rapidly gaining attention for their clinical potential as they present distinct advantages over traditional antibiotics. Antimicrobial peptides are found in all forms of life and demonstrate a pivotal role in the innate immune system. Many antimicrobial peptides are evolutionarily conserved, with limited propensity for resistance. Additionally, chemical modifications to the peptide backbone can be used to improve biological activity and stability and reduce toxicity. This review details the therapeutic potential of peptide-based antimicrobials, as well as the challenges needed to overcome in order for clinical translation. We explore the proposed mechanisms of activity, design of synthetic biomimics, and how this novel class of antimicrobial compound may address the need for effective antibiotics. Finally, we discuss commercially available peptide-based antimicrobials and antimicrobial peptides in clinical trials.

Numerous procedures have been described for the operative management of acromioclavicular joint injuries, but surprisingly little information is available on the ultimate mechanical behavior of the native coracoclavicular ligament complex or on the various methods of reconstruction. We tested 19 fresh-frozen cadaveric bone-ligament-bone preparations of the coracoclavicular ligament in uniaxial tension at 25 mm/min until failure. Seven specimens were left intact, six had the trapezoid ligament sectioned, and six had the conoid ligament sectioned. Reconstruction of the coracoclavicular ligament was achieved using coracoacromial ligament transfers, woven polyester slings, suture anchors, and Bosworth screws; all reconstructions were also tested to failure. The intact coracoclavicular ligament failed by avulsion or midsubstance tear at 500 (134) N, with a stiffness of 103 (30) N/mm and elongation to failure of 7.7 (1.9) mm. There was no significant difference between the contributions of the conoid or trapezoid ligaments in this loading configuration. Coracoclavicular slings and suture anchors provided strength similar to that of the coracoclavicular ligament, but with significantly greater deformations (14 to 26 mm). Screw fixation resulted in comparable stiffness and superior strength to the coracoclavicular ligament, but only if bicortical purchase was obtained. Coracoacromial ligament transfers were the weakest and least stiff, and augmentation with another form of coracoclavicular fixation is recommended. These results provide a useful baseline for comparison of the initial performance of reconstructive techniques with the performance of the native coracoclavicular ligament.

Calcium sulfate, plaster of Paris, has a long clinical history for use as a bone graft substitute in various skeletal sites. The current authors examined the in vivo response of calcium sulfate pellets alone or in combination with autogenous bone graft in a bilateral critical-size distal femoral cancellous defect in an adult sheep model. New thick bone formation was seen in defects filled with calcium sulfate pellets alone. Increased immunostaining for bone morphogenetic protein-2, bone morphogenetic protein-7, transforming growth factor-β, and platelet derived growth factor was seen in defects filled with calcium sulfate pellets alone and in combination with autograft. The local acidity during calcium sulfate resorption is proposed as a possible in vivo mechanism for this type of material.