Tyrosinase inhibitors have become increasingly important targets for hyperpigmentation disease treatment. Kojic monooleate (KMO), synthesized from the esterification of kojic acid and oleic acid, has shown a better depigmenting effect than kojic acid. In this study, the process parameters include the speed of high shear, the time of high shear and the speed of the stirrer in the production of nanoemulsion containing KMO was optimized using Response Surface Methodology (RSM), as well as evaluated in terms of its physicochemical properties, safety and efficacy. The optimized condition for the formulation of KMO nanoemulsion was 8.04 min (time of high shear), 4905.42 rpm (speed of high shear), and 271.77 rpm (speed of stirrer), which resulted in a droplet size of 103.97 nm. An analysis of variance (ANOVA) showed that the fitness of the quadratic polynomial fit the experimental data with large F-values (148.79) and small p-values (p < 0.0001) and an insignificant lack of fit. The optimized nanoemulsion containing KMO with a pH value of 5.75, showed a high conductivity value (3.98 mS/cm), which indicated that the nanoemulsion containing KMO was identified as an oil-in-water type of nanoemulsion. The nanoemulsion remains stable (no phase separation) under a centrifugation test and displays accelerated stability during storage at 4, 25 and 45 °C over 90 days. The cytotoxicity assay showed that the optimized nanoemulsion was less toxic, with a 50% inhibition of cell viability (IC₅₀) > 500 μg/mL, and that it can inhibit 67.12% of tyrosinase activity. This study reveals that KMO is a promising candidate for the development of a safe cosmetic agent to prevent hyperpigmentation.

Emerging dye pollution from textile industrial effluents is becoming more challenging for researchers worldwide. The contamination of water by dye effluents affects the living organisms in an ecosystem. Methylene blue (MB) and malachite green (MG) are soluble dyes with a high colour intensity even at low concentration and are hazardous to living organisms. The adsorption method is used in most wastewater plants for the removal of organic pollutants as it is cost-effective, has a high adsorption capacity, and good mechanical stabilities. In this study, a composite adsorbent was prepared by impregnating iron modified silica (FMS) onto polyurethane (PU) foam to produce an iron modified silica/polyurethane (FMS/PU) composite. The composite adsorbent was utilised in batch adsorption of the cationic dyes MB and MG. The effect of adsorption parameters such as the adsorbent load, pH, initial dye concentration, and contact time were discussed. Adsorption kinetics and isotherm were implemented to understand the adsorption mechanism for both dyes. It was found that the adsorption of MB and MG followed the pseudo-second order model. The Langmuir model showed a better fit than the Freundlich model for the adsorption of MB and MG, indicating that the adsorption occurred via the monolayer adsorption system. The maximum adsorption capacity of the FMS/PU obtained for MB was 31.7 mg/g, while for MG, it was 34.3 mg/g. The thermodynamic study revealed that the adsorption of MB and MG were exothermic and spontaneous at room temperature. In addition, the regeneration of FMS/PU was conducted to investigate the composite efficiency in adsorbing dyes for several cycles. The results showed that the FMS/PU composite could be regenerated up to four times when the regeneration efficiency dropped drastically to less than 20.0%. The impregnation of FMS onto PU foam also minimised the adsorbent loss into the environment.

An oil in water (O/W) nanoemulsion formulation containing kojic monooleate (KMO) in thin film system was developed. Response surface methodology (RSM) was used to optimize and analyzed the effect of three variables, namely concentration of polyvinyl alcohol (PVA) (20–30% w/w), concentration of propylene glycol (PG) (1–10% w/w), and shear rate of high shear homogenizer (3000–9000 rpm) on droplet size as a response, while other compositions remained constant such as KMO (10.0% w/w), Tween 80 (3.19% w/w), castor oil (3.74% w/w), xanthan gum (0.70% w/w), and germall plus (0.7% w/w, PG (and) diazolidinyl urea (and) iodopropynyl butylcarbamate). The optimized KMO nanoemulsion formulation with desirable criteria was PVA (27.61% w/w) and PG (1.05% w/w), and shear rate (8656.17 rpm) with a predicted droplet size (110.21 nm) and actual droplet size (105.93 nm) with a residual standard error (RSE) of less than 2.0% was obtained. Analysis of variance (ANOVA) showed that the fitness of the quadratic polynomial fit the experimental data with a F-value of 65.30, p–value of p < 0.0001, and a non-significant lack-of-fit. The optimized KMO formulation shows the desired criteria of the thin film system and the physicochemical properties (Zeta potential −37.37 mV, PDI 0.13, pH 4.74) and stability at four different conditions indicate its suitability for cosmeceutical applications.