This work focuses mainly on environmental concern and protection through providing beneficial use of waste biomass from water hyacinth to produce economical nano-magnetic adsorbent material-efficient for facile oil spill separation via an external magnetic field. The water hyacinth roots showed higher oil spills adsorption affinity of 2.2 g/g compared with 1.2 g/g for shoots. Nano-activated carbon was successfully extracted from the roots of water hyacinth after alkaline activation and followed by zinc chloride treatment before its carbonization. Nano-magnetite was induced into the activated carbonized nanomaterials to synthesized nano-magnetic activated carbon hybrid material (NMAC). X-ray diffraction elucidated the crystalline nature of both extracted activated carbon from water hyacinth and its magnetic hybrid material. Scanning electron microscopic micrographs implied the nano-size of both prepared activated carbon and the magnetite hybrid materials. The magnetic properties of the fabricated nano-magnetic activated carbon were evaluated using the vibrating sample magnetometer. The magnetic nano-hybrid material recorded a maximum oil adsorption affinity of 30.2 g oil/g. The optimum oil spill of 80% was established after 60 min in the presence of 1 g/L of magnetic nano-hybrid. The magnetic nano-hybrid material that absorbs oil spills was separated from the treatment media easily using an external magnetic field.

This reported work aims to fabricate an eco-friendly Zr bio-based MOF and assessment its adsorption efficiency towards the cationic and anionic dye pollutants including methylene blue (MB) and direct red 81 (DR-81), respectively. Also, its adsorption tendency for the highly toxic heavy metal of hexavalent chromium (Cr(VI)) was compared with dyes. The adsorption performance of bio-MOF showed that the maximum monolayer adsorption capacities were recorded as 79.799 mg/g for MB, 36.071 mg/g for DR-81, and 19.012 mg/g for Cr(VI). Meanwhile, the optimum dosage of as-synthesized MIP-202 bio-MOF was 0.5, 1, and 2 g L⁻¹ for MB, DR-81, and Cr(VI), respectively. Thermodynamic analysis demonstrated the spontaneous, thermodynamically, and endothermic nature of the decontamination processes onto the fabricated Zr bio-based MOF. The adsorption data were fitted by Langmuir isotherm model compared with Freundlich and Temkin models for all studied water pollutants. Pseudo-second-order kinetic model was a fit model for description of the adsorption kinetics of the different cationic and anionic pollutants onto Zr bio-based MOF. These outcomes indicated that Zr bio-based MOF has potential application for adsorption of different types of industrial water pollutants including cationic and anionic dyes and heavy metals.

An efficient, environmentally compatible and highly porous, silver surface-modified photocatalytic zinc oxide/cellulose acetate/ polypyrrole ZnO/CA/Ppy hybrid nanofibers matrix was fabricated using an electrospinning technique. Electrospinning parameters such as solution flow rate, applied voltage and the distance between needles to collector were optimized. The optimum homogenous and uniform ZnO/CA/Ppy polymeric composite nanofiber was fabricated through the dispersion of 0.05% wt ZnO into the dissolved hybrid polymeric solution with an average nanofiber diameter ranged between 125 and 170 nm. The fabricated ZnO-polymeric nanofiber was further surface-immobilized with silver nanoparticles to enhance its photocatalytic activity through the reduction of the nanofiber bandgap. A comparative study between ZnO polymeric nanofiber before and after silver immobilization was investigated using X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) and thermal gravimetric analysis (TGA). The photocatalytic degradation efficiency of the two different prepared nanofibers before and after nanosilver immobilization for malachite green (MG) dye was compared against various experimental parameters. The optimum degradation efficiency of nanosilver surface-modified ZnO-polymeric nanofibers was recorded as 93.5% for malachite green dye after 1 h compared with 63% for ZnO-polymeric nanofibers.

Nano-activated carbon (NAC) prepared from El-Maghara mine coal were modified with nitric acid solution. Their physico-chemical properties were investigated in terms of methylene blue (MB) adsorption, FTIR, and metal adsorption. Upon oxidation of the AC_S with nitric acid, surface oxide groups were observed in the FTIR spectra by absorption peaks at 1750–1250 cm⁻¹. The optimum processes parameters include HNO₃/AC ratio (wt./wt.) of 20, oxidation time of 2 h, and the concentration of HNO₃ of 10% reaching the maximum adsorption capacity of MB dye. Also, the prepared NAC was characterized by SEM, EDX, TEM, Raman Spectroscopy, and BET analyses. The batch adsorption of MB dye from solution was used for monitoring the behavior of the most proper produced NAC. Equilibrium isotherms of MB dye adsorption on NAC materials were acquired and the results discussed in relation to their surface chemistry. Langmuir model recorded the best interpretation of the dye adsorption data. Also, NAC was evaluated for simultaneous adsorption of six different metal ions (Fe²⁺, Ni²⁺, Mn²⁺, Pb²⁺, Cu²⁺, and Zn²⁺) that represented contaminates in petrochemical industrial wastewater. The results indicated that the extracted NAC from El-Maghara mine coal is considered as an efficient low-cost adsorbent material for remediation in both basic dyes and metal ions from the polluted solutions.

Nano-ZnO has been successfully implemented in particles, rods, and tubes nanostructures via sol-gel and hydrothermal techniques. The variation of the different preparation parameters such as reaction temperature, time, and stabilizer agents was optimized to attain different morphological structures. The influence of the microwave annealing process on ZnO crystallinity, surface area, and morphological structure was monitored using XRD, BET, and SEM techniques, respectively. The antimicrobial activity of zinc oxide produced in nanotubes structure was examined against four different multidrug resistant bacteria: Gram-positive (Staphylococcus aureusandBacillus subtilis) and Gram-negative (Escherichia coliandPseudomonas aeruginosa) strains. The activity of produced nano-ZnO was determined by disc diffusion technique and the results revealed that ZnO nanotubes recorded high activity against the studied strains due to their high surface area equivalent to 17.8 m²/g. The minimum inhibitory concentration (MIC) of ZnO nanotubes showed that the low concentrations of ZnO nanotubes could be a substitution for the commercial antibiotics when approached in suitable formula. Although the annealing process of ZnO improves the degree of material crystallinity, however, it declines its surface area and consequently its antimicrobial activity.