There is a strong public concern about plastic waste, which promotes the development of new biobased materials. The benefit of using microbial biomass for new developments is that it is a completely renewable source of polymers, which is not limited to climate conditions or may cause deforestation, as biopolymers come from vegetal biomass. The present review is focused on the use of microbial biomass and its derivatives as sources of biopolymers to form new materials. Yeast and fungal biomass are low-cost and abundant sources of biopolymers with high promising properties for the development of biodegradable materials, while milk and water kefir grains, composed by kefiran and dextran, respectively, produce films with very good optical and mechanical properties. The reasons for considering microbial cellulose as an attractive biobased material are the conformational structure and enhanced properties compared to plant cellulose. Kombucha tea, a probiotic fermented sparkling beverage, produces a floating membrane that has been identified as bacterial cellulose as a side stream during this fermentation. The results shown in this review demonstrated the good performance of microbial biomass to form new materials, with enhanced functional properties for different applications.

Innovative and sustainable all-cellulose composites (ACCs) can be obtained by partial dissolution of cellulosic fibers and regeneration of the dissolved fraction. Among cellulose solvents, sodium hydroxide/urea solutions are recognized as promising low-environmental impact systems. In this work, filter paper (FP) was dissolved with a 7 wt% NaOH/12 wt% urea aqueous solution, kept at −18 °C for different time intervals, regenerated with distilled water and finally dried under different conditions. The developed films were characterized in terms of morphology, porosity, optical properties, crystalline structure, hydration and mechanical properties. The porosity of the composites decreased with dissolution time due to the progressive filling of voids as the cellulosic fibers’ surface skin layer was dissolved and regenerated. Samples treated for 4 h showed the minimum values of porosity and opacity, high hydration and a substantial change from cellulose I to cellulose II. Hot pressing during drying led to relevant improvements in ACCs stiffness and strength values.

The use of biopolymeric materials is restricted for some applications due to their deficient properties in comparison to synthetic polymers. Blending different biopolymers is an alternative approach to overcome these limitations. In this study, we developed new biopolymeric blend materials based on the entire biomasses of water kefir grains and yeast. Film-forming dispersions with varying ratios of water kefir to yeast (100/0, 75/25, 50/50 25/75 and 0/100) underwent ultrasonic homogenisation and thermal treatment, resulting in homogeneous dispersions with pseudoplastic behaviour and interaction between both biomasses. Films obtained by casting had a continuous microstructure without cracks or phase separation. Infrared spectroscopy revealed the interaction between the blend components, leading to a homogeneous matrix. As the water kefir content in the film increased, transparency, thermal stability, glass transition temperature and elongation at break also increased. The thermogravimetric analyses and the mechanical tests showed that the combination of water kefir and yeast biomasses resulted in stronger interpolymeric interactions compared to single biomass films. The ratio of the components did not drastically alter hydration and water transport. Our results revealed that blending water kefir grains and yeast biomasses enhanced thermal and mechanical properties. These studies provided evidence that the developed materials are suitable candidates for food packaging applications.