Nanocomposite gels containing chitosan as a network polymer and chitin nanowhiskers as reinforcing fillers were prepared by cross-linking with the blocked isocyanate hexamethylene-1,6-di-(aminocarboxysulfonate) (HDS). Young’s modulus and stress at break of the nanocomposite gels increased to maximum values of 169 and 135 kPa, respectively, with increase in whisker content up to 13.3%, whereas the degree of swelling decreased from 357 to 33.0.

We describe the preparation of cellulose nanofibrous material directly from cellulose solution via electrospinning. The resulting nanofiber is composed of pure cellulose. The spinning procedure can be performed under ambient conditions at room temperature without post-spun treatment. By mixing drugs with the pre-spun cellulose solution, followed by electrospinning, the drug-loaded nanofiber was prepared and the releasing properties were examined with respect to biomedical applications.