This paper reviews our work on the application of ultrafast pulsed laser micro/nanoprocessing for the three-dimensional (3D) biomimetic modification of materials surfaces. It is shown that the artificial surfaces obtained by femtosecond-laser processing of Si in reactive gas atmosphere exhibit roughness at both micro- and nanoscales that mimics the hierarchical morphology of natural surfaces. Along with the spatial control of the topology, defining surface chemistry provides materials exhibiting notable wetting characteristics which are potentially useful for open microfluidic applications. Depending on the functional coating deposited on the laser patterned 3D structures, we can achieve artificial surfaces that are (a) of extremely low surface energy, thus water-repellent and self-cleaned, and (b) responsive, i.e., showing the ability to change their surface energy in response to different external stimuli such as light, electric field, and $p\text{H}$ . Moreover, the behavior of different kinds of cells cultured on laser engineered substrates of various wettabilities was investigated. Experiments showed that it is possible to preferentially tune cell adhesion and growth through choosing proper combinations of surface topography and chemistry. It is concluded that the laser textured 3D micro/nano-Si surfaces with controllability of roughness ratio and surface chemistry can advantageously serve as a novel means to elucidate the 3D cell-scaffold interactions for tissue engineering applications.

This study reports on the production of high-resolution 3D structures of polylactide-based materials via multi-photon polymerization and explores their use as neural tissue engineering scaffolds. To achieve this, a liquid polylactide resin was synthesized in house and rendered photocurable via attaching methacrylate groups to the hydroxyl end groups of the small molecular weight prepolymer. This resin cures easily under UV irradiation, using a mercury lamp, and under femtosecond IR irradiation. The results showed that the photocurable polylactide (PLA) resin can be readily structured via direct laser write (DLW) with a femtosecond Ti:sapphire laser and submicrometer structures can be produced. The maximum resolution achieved is 800 nm. Neuroblastoma cells were grown on thin films of the cured PLA material, and cell viability and proliferation assays revealed good biocompatibility of the material. Additionally, PC12 and NG108-15 neuroblastoma growth on bespoke scaffolds was studied in more detail to assess potential applications for neuronal implants of this material.