Poly(lactic acid) (PLA) and polypropylene (PP) were comparatively investigated as matrices for injection-moulded composites containing small (1–3 wt%) amounts of short sisal fibre. The morphology, thermal and dynamic mechanical properties, as well as degradation characteristics were investigated. The scanning electron microscopy (SEM) micrographs of the composites show more intimate contact and better interaction between the fibres and PLA, compared to PP. This improved interaction was confirmed by the Fourier-transform infrared (FTIR) spectroscopy results which showed the presence of hydrogen bonding interaction between PLA and the fibres. The thermal stability (as determined through thermogravimetric analysis [TGA]) of both polymers increased with increasing fibre content, with a more significant improvement in the case of PP. The differential scanning calorimetry (DSC) results showed a significant influence of the fibres on the cold crystallization and melting behaviour of PLA, even at the low fibre contents of 1–3%. The influence of the fibres on the melting characteristics of the PP was negligible, but it had a significant influence on the nonisothermal crystallization temperature range. Both the storage and loss moduli of the PLA decreased with increasing fibre content below the glass transition of PLA, but the influence on the loss modulus was more significant. The dynamic mechanical analysis (DMA) results clearly show cold crystallization of PLA around 110°C, and the presence of fibres gave rise to higher modulus values between the cold crystallization and melting of the PLA. The presence of fibres also had an influence on the dynamic mechanical properties of PP. This article further describes basic biodegradation observations for the investigated samples.

Scientists from various different fields use organo-trialkoxysilanes and tetraalkoxysilanes in a number of applications. The silica-based materials are sometimes synthesized without a good understanding of the underlying reaction kinetics. This literature review attempts to be a comprehensive and more technical article in which the kinetics of alkoxysilanes polymerization are discussed. The kinetics of polymerization are controlled by primary factors, such as catalysts, water/silane ratio, pH, and organo-functional groups, while secondary factors, such as temperature, solvent, ionic strength, leaving group, and silane concentration, also have an influence on the reaction rates. Experiments to find correlations between these factors and reaction rates are restricted to certain conditions and most of them disregard the properties of the solvent. In this review, polymerization kinetics are discussed in the first two sections, with the first section covering early stage reactions when the reaction medium is homogenous, and the second section covering when phase separation occurs and the reaction medium becomes heterogeneous. Nuclear magnetic resonance (NMR) spectroscopy and other techniques are discussed in the third section. The last section summarizes the study of reaction mechanisms by using ab initio and Density Functional Theory (DFT) methods alone, and in combination with molecular dynamics (MD) or Monte Carlo (MC) methods.

This paper focuses on the crystalline structure of injection moulding grade poly(lactic acid) (PLA) and the effect of crystalline structure on the processing. The research is induced by the significant differences in crystallinity of the pure PLA resin, and the injection moulded product, and thus the reprocessing of PLA products. 2 mm thick PLA sheets were injection moulded and re-crystallized in a conventional oven at 60–140°C, for 10–60 minutes to achieve various crystalline contents. The properties of these sheets were investigated by dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC), and wide angle X-ray diffraction (WAXD). In a processing plant the rejected parts are recycled and reused as raw material for further cycles, accordingly the various crystalline content PLA products were reprocessed as a resin, to investigate the processing itself. When PLA products are reprocessed, due to the adherent feature of amorphous PLA processing difficulties may occur. This adherent effect of the amorphous PLA was investigated and characterized