Purpose: This study aims to examine the impact of specific printing factors, such as layer height, line width and build orientation, on the overall quality of fused filament fabrication (FFF) 3D printed structures. The project also intends to use response surface methodology (RSM) to maximize ultimate tensile strength (UTS) while lowering surface roughness and printing time. Design/methodology/approach: This study used an FFF printer to fabricate samples of polylactic acid (PLA), which were then subjected to assessments of tensile strength and surface roughness. A tensile test was conducted under standardized conditions according to the ASTM D638 standard test method using the AG-50 kN Shimadzu Autograph. The Mitutoyo Surftest SJ-210, which utilizes a needle-tipped inductive method, was used to determine surface roughness. RSM was used for optimization. Findings: This work provides useful insights into how the printing parameters affect FFF 3D printed structures, which may be used to optimize the printing process and improve PLA-based 3D printed products' qualities. The determined optimal values for building orientation, layer height and line width were 0°, 0.1 mm and 0.6 mm, respectively. The total desirability value of 0.80 implies desirable outcomes, and good agreement between experimental and projected response values supports the suggested models. Originality/value: Previous RSM studies for 3D printing parameter optimization focused on mechanical properties or surface aspects, however, few examined multiple responses and their interactions. This study emphasizes the relevance of FFF parameters like line width, which are often overlooked but can dramatically impact printing quality. Mechanical properties, surface quality and printing time are integrated to comprehend optimization holistically.

The advent of additive manufacturing also referred to as 3D printing, has brought about substantial changes in the industrial domain, as it possesses the capability to fabricate intricate items with enhanced cost‐efficiency and productivity. Fused Filament Fabrication (FFF) is a 3D printing process that has gained significant popularity due to its versatile capabilities and cost‐effectiveness. This paper investigates the impact of the printing parameters on the tensile characteristics of Triply Periodic Minimal Surface (TPMS) manufactured using FFF 3D printing. TPMS patterns have unique geometric properties and potential applications, making them an intriguing subject of study. The behavior of three different TPMS lattices with three printing parameters is investigated. Finding the best testing settings is done with the Taguchi method, and the data is analyzed with the Analysis of Variance (ANOVA) test. TPMS pattern was found to be the most effective parameter with 83.78%. While the highest strength was obtained in Schwarz diamond, the highest energy absorption was observed in the Gyroid structure. The contributions of printing parameters to tensile strength are line thickness, printing speed, and layer height, respectively. As line width and printing speed increase, both energy absorption and strength increase. Therefore, 0.40 mm line width and 60 mm/s printing speed give optimum values. When considered for energy absorption, the optimum value is 0.20 mm layer height, while when considered for strength, 0.10 mm layer height is the optimum value. The findings emphasize the importance of optimizing printing parameters for desired mechanical characteristics in 3D printed components and highlight the potential of TPMS structures in various applications. This research contributes to the growing knowledge in additive manufacturing and provides insights into optimizing FFF 3D printing for improved mechanical performance.