In the search for eco-friendly and resource-efficient alternatives to conventional building materials, agricultural residues are gaining increasing attention as reinforcements in cement-based composites. This study investigates the potential of walnut shell particles (WSPs), a lignocellulosic bio-product, as a sustainable reinforcing agent in walnut shell cement boards (WSCBs). Using super white cement (SWC) as a binder, boards were manufactured with WSP content ranging from 10% to 50% by weight, targeting a density of 1300 kg/m³, a 10 mm thickness, and a water-to-cement ratio of 0.6:1. The mixtures were cold-pressed at ambient temperature using a hydraulic press at 3 MPa for 24 h, followed by curing for 28 days under ambient conditions. Physical properties such as density, water absorption, and thickness swelling were assessed, along with mechanical performance, through flexural testing. Fracture surfaces and internal microstructures were examined using scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). Functional groups and chemical reactions were monitored using FTIR, while thermal analysis (TGA and DSC), as well as measurements of thermal conductivity and resistance, provided comprehensive insights into the thermal behavior, insulating performance, and energy efficiency potential of the boards. Results demonstrate that the board with 30% WSP exhibited an optimal balance of physical and mechanical properties, achieving a 24 h water absorption of 14.05% and a modulus of rupture (MOR) of 6.53 MPa, making it suitable for non-structural applications. The board with 50% WSP exhibited the best thermal insulation performance, with a low thermal conductivity of 0.079 W/m·K. These findings highlight the potential of recycled agricultural materials in enhancing building materials’ performance, contributing to sustainable, eco-friendly construction practices.

The growing demand for sustainable building materials, amid escalating costs, has spurred interest in alternative solutions such as wood cement composites. This study explores the feasibility of producing wood cement boards (WCBs) using locally sourced cedar sawdust as a reinforcing agent. Boards with a thickness of 10 mm and a target density of 1200 kg/m³ were manufactured under pressures ranging from 2 to 6 MPa for 24 h. Cedar sawdust, used as raw and untreated material, was incorporated into the mixture as a partial substitute for cement in varying proportions, ranging from 10% to 25% (by weight). The WCBs were cured for 28 days under ambient conditions. Physical properties including density, water absorption (WA), and thickness swelling (TS) were assessed, along with mechanical properties through flexural tests. The results showed that increasing cedar sawdust content decreased both density and mechanical performance while increasing WA and TS. Microstructural analysis (SEM and EDS) revealed significant porosity at higher sawdust contents, while lower contents had better matrix–reinforcement cohesion. Additionally, substantial levels of calcium and silicon were detected on the sawdust surface, indicating stabilized cement hydration products. These findings, supported by thermal (TGA and DSC) and FTIR analyses, clearly demonstrate that cement boards with 10% cedar sawdust exhibit favorable properties for non-structural applications, such as wall and partition cladding.