This article focuses on a systematic study of a Ti-6Al-4V alloy in order to extensively characterize the main mechanical properties at the macro-, micro- and submicrometric length scale under different stress fields. Hardness, elastic modulus, true stress–strain curves and strain-hardening exponent are correlated with the intrinsic properties of the α- and β-phases that constitute this alloy. A systematic characterization process followed, considering the anisotropic effect on both orthogonal crystallographic directions, as well as determining the intrinsic properties for the α-phase. An analytical relationship was established between the flow stress determined under different stress fields, testing geometries and length scales, highlighting that it is possible to estimate flow stress under compression and/or tensile loading from the composite hardness value obtained by instrumented nanoindentation testing.

Nanocomposites and a composite based on poly(butylene adipate-co-terephthalate) (PBAT) were synthesized using commercial copper nanoparticles (Cu-NPs), copper/cuprous oxide nanoparticles (Cu|Cu2O-NPs), and copper sulfate (CuSO4), respectively. The Cu|Cu2O-NPs were synthesized using chemical reduction and characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The synthesis of Cu|Cu2O-NPs yielded a mixture of Cu and Cu2O, with metal Cu having a spherical morphology of approximately 40 nm in diameter and Cu2O with a diameter of 150 nm. To prepare the nanocomposites (NCs) and the composite material (MC), the NPs and the CuSO4 salt were incorporated into the PBAT matrix in concentrations of 1, 3, and 5% p/p via an ex situ method. Fourier transform infrared spectroscopy (FTIR), a tensile test, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and agar diffusion assays were used for structural, thermomechanical, and antimicrobial characterization. Results showed that the reinforcements did not modify the chemical structure of the PBAT and only slightly increased the percentage of crystallization. The mechanical and thermal properties of the PBAT did not change much with the addition of fillers, except for a slight increase in tensile strength and thermal stability, respectively. The agar diffusion antimicrobial assays showed that the NCs and MCs had good inhibitory responses against the nonresistant strains Enterococcus faecalis, Streptococcus mutans, and Staphylococcus aureus. The MCs based on CuSO4 had the highest biocidal effect, even against the resistant bacteria Acinetobacter baumannii.