The presence of the crystalline regions in poly(vinyl alcohol) coating films acts as barrier clusters forcing the gas molecules to diffuse in a longer pathway in the amorphous region of the polymer, where diffusivity and solubility are promoted in comparison. Evaluating the influence of crystalline regions on the oxygen barrier property of a semi-crystalline polymer is thus essential to prepare better coating films. Poly(vinyl alcohol) coating films with varying induced crystallinity were prepared on a polyethylene terephthalate (PET) substrate by drying at different annealing temperatures for 10 min. The coating films were first delaminated from the PET substrate and then characterized using Fourier transform infrared (FTIR) spectroscopy, differential scanning calorimetry (DSC), and X-ray diffraction (XRD) techniques to determine and confirm the induced percentage of crystallinity. The barrier performance of the coating films, i.e., the oxygen transmission rate (OTR), was measured at room temperature. Results showed a decrease in the OTR values of poly(vinyl alcohol) film with an increase in the degree of crystallinity of the polymer matrix. Tortuosity-based models, i.e., modified Nielsen models, were adopted to predict the barrier property of the semi-crystalline PVOH film with uniform or randomly distributed crystallites. A modified Nielsen model for orderly distributed crystallites with an aspect ratio of 3.4 and for randomly distributed crystallites with an aspect ratio of 10.4 resulted in a good correlation with the experimental observation. For the randomly distributed crystallites, lower absolute average relative errors of 4.66, 4.45, and 5.79% were observed as compared to orderly distributed crystallites when the degree of crystallinity was obtained using FTIR, DSC, and XRD data, respectively.

The mechanical properties and chemical stability in water of self-supporting films made from aqueous solutions of starch and lignin, and the barrier properties of paperboard coated with solutions of these polymers have been studied. The dissolution of starch from the starch-lignin films in contact with the model liquids was decreased significantly when lignin was added to the starch films. The addition of ammonium zirconium carbonate (AZC) to the formulations as a crosslinking agent substantially increased the storage modulus of the starch-lignin films, which indicated that crosslinking had occurred. The addition of AZC to the formulations also led to a decrease in dissolution of both starch and lignin from the starch-lignin films in contact with model liquids. The effect of AZC on the water stability of the films was greater when the pH of the starch-lignin-AZC solution was adjusted with ammonia rather than NaOH. The addition of NH₄Cl solution as a presumed catalyst to the recipe when the pH adjustment was performed with NaOH did not improve the effect of AZC on the water stability of the films. The water vapour transmission rate of the coated paperboard decreased slightly when AZC was added to the coating formulation.

One severe weakness of most biopolymers, in terms of their use as packaging materials, is their relatively high solubility in water. The addition of kraft lignin to starch coating formulations has been shown to reduce the water solubility of starch in dry coatings. However, lignin may also migrate into aqueous solutions. For this paper, kraft lignin isolated using the LignoBoost process was used in order to examine the effect of pH level on the solubility of lignin with and without ammonium zirconium carbonate (AZC). Machine-glazed (MG) paper was coated in a pilot coating machine, with the moving substrate at high speed, and laboratory-coated samples were used as a reference when measuring defects (number of pinholes). Kraft lignin became soluble in water at lower pH levels when starch was added to the solution, due to the interactions between starch and lignin. This made it possible to lower the pH of the coating solutions, resulting in increased water stability of the dry samples; that is, the migration of lignin to the model liquids decreased when the pH of the coating solutions was reduced. No significant difference was observed in the water vapor transmission rate (WVTR) between high and low pH for the pilot-coated samples. The addition of AZC to the formulation reduced the migration of lignin from the coatings to the model liquids and led to an increase in the water contact angle, but also increased the number of pinholes in the pilot-coated samples.