Calcium‐based stabilizer materials (CSMs) exhibit pozzolanic properties which improve the properties of clayey soils by hydration, cation exchange, flocculation, pozzolanic reaction, and carbonation. In this comprehensive review, comprising over past three decades from 1990 to 2019, a mechanistic literature of expansive soil stabilization by incorporating CSMs is presented by reviewing 183 published research articles. The advantages and disadvantages of CSMs as the ground stabilizing agent are succinctly presented, and the major outcomes of physicochemical effects on soil properties are discussed in detail. After blending with CSM, the main and interaction effects on soil properties with focus on chemical processes such as X‐ray fluorescence, X‐ray diffraction analyses, and microstructure interaction by using scanning electron microscopy and thermogravimetric analysis have been reviewed in light of findings of past researchers. This work will help geotechnical engineers to opt for suitable CSM in the field of geoenvironmental engineering in committing to sustainable construction of civil engineering structures over expansive soils.

Expansive/swell‐shrink soils exhibit high plasticity and low strength, which lead to settlement and instability of lightly loaded structures. These problematic soils contain various swelling clay minerals that are unsuitable for engineering requirements. In an attempt to counter the treacherous damage of such soils in modern geotechnical engineering, efforts are underway to utilize environmentally friendly and sustainable waste materials as stabilizers. This study evaluates the strength and consolidation characteristics of expansive soils treated with marble dust (MD) and rice husk ash (RHA) through a multitude of laboratory tests, including consistency limits, compaction, uniaxial compression strength (UCS), and consolidation tests. By using X‐ray diffraction (XRD) and scanning electron microscopy (SEM) analyses, the effect of curing on UCS after 3, 7, 14, 28, 56, and 112 days was studied from the standpoint of microstructural changes. Also, the long‐term strength development of treated soils was analyzed in terms of the interactive response of impacting factors with the assistance of a series of ANN‐based sensitivity analyses. It is found from the results that the addition of MD and RHA lowered down the water holding capacity, thereby causing a reduction in soil plasticity (by 21% for MD and 14.5% for RHA) and optimum water content (by 2% for MD and increased by 6% for RHA) along with an increase in the UCS (for 8% MD from 97 kPa to 471 kPa and for 10% RHA from 211 kPa to 665 kPa, after 3 days and 112 days of curing, respectively). Moreover, from the oedometer test results, m_v initially increased up to 6% dosage and then dropped with further increase in the preconsolidation pressure. Furthermore, the compression index dropped with an increase in the preconsolidation pressure and addition of MD/RHA, while the coefficient of permeability (k) of RHA stabilized soil was higher than that of MD‐treated samples for almost all dosage levels. The formation of the fibrous cementitious compounds (C‐S‐H; C‐A‐H) increased at optimum additive dosage after 7 days and at higher curing periods. Hence, the use of 10% RHA and 12% MD as replacement of the expansive soil is recommended for higher efficacy. This research would be helpful in reducing the impacts created by the disposal of both expansive soil and industrial and agricultural waste materials.

This paper evaluates the suitability of sugarcane bagasse ash (SCBA) and waste marble dust (WMD) on the geotechnical properties of Palygorskite‐rich expansive clays located in northwest Pakistan. These problematic soils exhibit undesirable characteristics which greatly affect the pavements, boundary walls, slab‐on‐grade members, and other civil engineering infrastructures. A series of geotechnical tests were performed on soil specimens using prescribed percentages of the aforementioned Ca‐based stabilizer materials (CSMs). The investigation includes X‐Ray Diffraction (XRD) Analysis, Scanning Electron Microscopy (SEM), X‐Ray Fluorescence (XRF) tests, and physicomechanical properties such as moisture‐density relationship, Atterberg’s limits, swell pressure, and an ANN‐based sensitivity analyses of overall swell pressure development. The outcomes of these experimental investigations showed that the addition of CSMs into the expansive soils increased to 4% SCBA and 10% WMD, the plasticity index reduced by 30% and 49%, the volumetric swell decreased from approximately 49% to 86% and 63%, and the swelling pressure reduction was from 189 kPa to 120 kPa and 160 kPa (about 15% and 36%), respectively. It is interesting to note that replacement with specified CSM accelerated the strength of soil at extended curing periods and the optimum improvement in the strength behavior of the soil was also recorded. Moreover, with addition of the respective CSMs, the compactability and strength characteristics were ameliorated, while plasticity was significantly lowered. Given the amount of SCBA and WMD produced annually, their utilization for the stabilization of problematic soils, even in relatively low concentrations, could potentially have a substantial impact on the sustainable reuse of these waste materials.