Nanotechnology involves the study of nature at a very small scale, searching new properties and applications. The development of this area of knowledge affects greatly both biotechnology and medicine disciplines. The use of materials at the nanoscale, in particular magnetic nanoparticles, is currently a prominent topic in healthcare and life science. Due to their size-tunable physical and chemical properties, magnetic nanoparticles have demonstrated a wide range of applications ranging from medical diagnosis to treatment. Combining a high saturation magnetization with a properly functionalized surface, magnetic nanoparticles are provided with enhanced functionality that allows them to selectively attach to target cells or tissues and play their therapeutic role in them. In particular, iron oxide nanoparticles are being actively investigated to achieve highly efficient carcinogenic cell destruction through magnetic hyperthermia treatments. Hyperthermia in different approaches has been used combined with radiotherapy during the last decades, however, serious harmful secondary effects have been found in healthy tissues to be associated with these treatments. In this framework, nanotechnology provides a novel and original solution with magnetic hyperthermia, which is based on the use of magnetic nanoparticles to remotely induce local heat when a radiofrequency magnetic field is applied, provoking a temperature increase in those tissues and organs where the tumoral cells are present. Therefore, one important factor that determines the efficiency of this technique is the ability of magnetic nanoparticles to be driven and accumulated in the desired area inside the body. With this aim, magnetic nanoparticles must be strategically surface functionalized to selectively target the injured cells and tissues.

Polymeric materials have been extensively explored in the field of nanomedicine; within them, poly lactic-co-glycolic acid (PLGA) holds a prominent position in micro- and nanotechnology due to its biocompatibility and controllable biodegradability. In this review we focus on the combination of PLGA with different inorganic nanomaterials in the form of nanocomposites to overcome the polymer’s limitations and extend its field of applications. We discuss their physicochemical properties and a variety of well-established synthesis methods for the preparation of different PLGA-based materials. Recent progress in the design and biomedical applications of PLGA-based materials are thoroughly discussed to provide a framework for future research.

Exceptional magnetic properties of magnetite, Fe₃O₄, nanoparticles make them one of the most intensively studied inorganic nanomaterials for biomedical applications. We report successful gram-scale syntheses, via hydrothermal route or controlled coprecipitation in an automated reactor, of colloidal Fe₃O₄ nanoparticles with sizes of 12.9 ± 5.9, 17.9 ± 4.4, and 19.8 ± 3.2 nm. To investigate structure–property relationships as a function of the synthetic procedure, we used multiple techniques to characterize the structure, phase composition, and magnetic behavior of these nanoparticles. For the iron oxide cores of these nanoparticles, powder X-ray diffraction and electron microscopy both confirm single-phase Fe₃O₄ composition. In addition to the core composition, the magnetic performance of nanoparticles in the 13–20 nm size range can be strongly influenced by the surface properties, which we analyzed by three complementary techniques. Raman scattering and X-ray photoelectron spectroscopy (XPS) measurements indicate overoxidation of nanoparticle surfaces, while transmission electron microscopy (TEM) shows no distinct core–shell structure. Considered together, Raman, XPS, and TEM observations suggest that our nanoparticles have a gradually varying nonstoichiometric Fe₃O_4+δ composition, which could be attributed to the formation of Fe₃O₄–γ-Fe₂O₃ solid solutions at their outermost surface. Detailed analyses by TEM reveal that the hydrothermally produced samples include single-domain nanocrystals coexisting with defective twinned and dimer nanoparticles, which form as a result of oriented-attachment crystal growth. All our nanoparticles exhibit superparamagnetic-like behavior with a characteristic blocking temperature above room temperature. We attribute the estimated saturation magnetization values up to 84.01 ± 0.25 emu/g at 300 K to the relatively large size of the nanoparticles (13–20 nm) coupled with the syntheses under elevated temperature; alternative explanations, such as surface-mediated effects, are not supported by our spectroscopy or microscopy measurements. For these colloids, the heating efficiency in magnetic hyperthermia correlates with their saturation magnetization, making them appealing for therapeutic and other biomedical applications that rely on high-performance nanoparticle-mediated hyperthermia.

In biomedicine, magnetic nanoparticles provide some attractive possibilities because they possess peculiar physical properties that permit their use in a wide range of applications. The concept of magnetic guidance basically spans from drug delivery and hyperthermia treatment of tumours, to tissue engineering, such as magneto-mechanical stimulation/activation of cell constructs and mechanosensitive ion channels, magnetic cell-seeding procedures, and controlled cell proliferation and differentiation. Accordingly, the aim of this study was to develop fully biodegradable and magnetic nanocomposite substrates for bone tissue engineering by embedding iron-doped hydroxyapatite (FeHA) nanoparticles in a poly(ε-caprolactone) (PCL) matrix. X-ray diffraction analyses enabled the demonstration that the phase composition and crystallinity of the magnetic FeHA were not affected by the process used to develop the nanocomposite substrates. The mechanical characterization performed through small punch tests has evidenced that inclusion of 10 per cent by weight of FeHA would represent an effective reinforcement. The inclusion of nanoparticles also improves the hydrophilicity of the substrates as evidenced by the lower values of water contact angle in comparison with those of neat PCL. The results from magnetic measurements confirmed the superparamagnetic character of the nanocomposite substrates, indicated by a very low coercive field, a saturation magnetization strictly proportional to the FeHA content and a strong history dependence in temperature sweeps. Regarding the biological performances, confocal laser scanning microscopy and AlamarBlue assay have provided qualitative and quantitative information on human mesenchymal stem cell adhesion and viability/proliferation, respectively, whereas the obtained ALP/DNA values have shown the ability of the nanocomposite substrates to support osteogenic differentiation.