In this work, electrochemical monitoring of stress corrosion cracking (SCC) behavior of a X70 steel in acidic synthetic soil solution during the slow strain rate test (SSRT) was performed by electrochemical noise (EN) using the conventional arrangement of symmetrical electrodes and electrochemical emission spectroscopy (EES) using the asymmetrical arrangement replacing the second working electrode for a platinum micro-cathode. The statistical method, fast Fourier transform, and discrete wavelet transform were used for analyzing the potential and current signals recorded by both arrangements. The results showed that EN arrangement was more effective to detect the crack initiation at a point close to yield strength despite stress-induced asymmetry in one of the electrodes. For the EES arrangement, the micro-cathode had a strong influence on the electrochemical noise of the current and potential under stress conditions. From the transient features, statistical parameters, and wavelet analysis, a discontinuous transgranular SCC mechanism was found. The resistance values obtained by EN measurements had better correlation with the electrochemical impedance spectroscopy results (EIS) than EES measurements.

In this research work, the influence of the electrolyte hydrodynamic conditions on the corrosion mechanism of the high-strength low-alloy (HSLA) X100 steel used in the petroleum transportation pipelines was analyzed. A Rotary Cylinder Electrode (RCE) was used to simulate the hydrodynamic conditions (1000 and 5000 rpm). Mechanical, microstructural and elemental characterization tests were performed on X100 steel, and the electrochemical impedance spectroscopy (EIS) technique was used to analyze the corrosion mechanism, while the morphology of the corrosion process on the corroded surfaces was obtained by scanning electronic microscopy (SEM). It was found that the increasing rotation rate (υ rot) generates a fully developed flow regime where the system was dominated by a mass transfer process and increases the kinetics of chemical and electrochemical reactions so there is an increase in the corrosion rate (CR). On the other hand, the adsorption of corrosion product films that limits the charge transfer process depended on the magnitude of the shear stress that can generate wear and roughness, as well as a greater number of anodic sites, leaving the metal exposure to the corrosive medium.