The use of untreated recycled water has negative effects in the flotation of zinc sulfide ores due to the presence of dissolved species, such as magnesium and calcium. Although it has been found that magnesium is a more potent depressant than calcium, it has not been investigated in this role or for the effect of adding sodium carbonate. The results of an investigation to evaluate the effect of magnesium on the hydrophobicity of Cu-activated sphalerite conditioned with Sodium Isopropyl Xanthate (SIPX) are presented. Zeta potential of natural and Cu-activated sphalerite as a function of the conditioning pH and Cu(II) concentration, respectively, was first evaluated. Later, the effect of pH and presence of magnesium on the contact angle of Cu-activated sphalerite conditioned with SIPX was studied; it was also evaluated the effect of sodium carbonate to counteract the effect of magnesium. Cu-activation enhances the zeta potential of sphalerite up to a concentration of 5 mg/L. Contact angle tests, thermodynamic simulation, and surface analysis showed that magnesium hydroxide precipitates on the sphalerite surface at pH 9.6, decreasing its hydrophobicity. Addition of sodium carbonate as alkalinizing agent precipitates the magnesium in the form of a species that remained dispersed in the bulk solution, favoring the contact angle of Cu-activated sphalerite and, consequently, its hydrophobicity. It is concluded that the use of sodium carbonate as alkalinizing agent favors the precipitation of magnesium as hydromagnesite (Mg₅(OH)₂(CO₃)₄∙4H₂O) instead of hydroxide allowing the recovery of sphalerite.

The presence of calcium sulfate in the process water during the coal flotation greatly influences the recovery and selectivity of the separation. The concentrations of calcium and sulfate ions modify mineral hydrophobicity by altering surface properties resulting in depression or activation of the mineral species. An investigation to evaluate the statistical significance of the effect of the pH and concentration of calcium and sulfate ions on coal flotation was carried out; for this purpose, a 2³ factorial design was implemented. A p-value < 0.05 was determined for the effect of calcium and sulfate ion concentrations, indicating that it is statistically significant. The interactions between factors (pH × calcium, pH × sulfate, calcium × sulfate and pH × calcium × sulfate) are also statistically significant, but the interaction between the concentration of calcium and sulfate ions has a notable influence according to the F statistic value. Employing 800 and 1920 mg/L of calcium and sulfate ions as experimental conditions yields a recovery of 90.4% with a concentrate containing 13% ash.

El zinc es un metal con diversas aplicaciones industriales que se puede obtener por la vía hidrometalúrgica y pirometalúrgica. En esta revisión se abordan los avances frente a la producción sostenible de este metal. Este enfoque implica la adopción de prácticas y procesos que minimicen el impacto ambiental y fomenten el uso responsable de los recursos. Asimismo, se exploran las principales aplicaciones del zinc y la demanda proyectada a futuro. Además, se revisa la obtención de zinc a partir de fuentes secundarias como pilas usadas, chatarra electrónica, aleaciones de zinc, entre otras. Dichos procesos introducen el concepto de minería urbana, el cual promueve la transición hacia una economía circular. El reciclaje representa una actividad económicamente viable y contribuye a disminuir el volumen de residuos enviados a las presas de jales.

La leonardita es un compuesto orgánico que contiene una cantidad significativa de sustancias húmicas. En la región carbonífera del estado de Coahuila, se puede encontrar este material en abundancia. Los fertilizantes a base de ácidos húmicos son efectivos para el tratamiento de suelos, además desempeñan un papel importante en diversos procesos bioquímicos. La presente investigación es un estudio exploratorio sobre la obtención de ácido húmico para su uso como fertilizante. Las pruebas de extracción se llevaron a cabo en medio alcalino, utilizando hidróxido de sodio (NaOH) como agente extractante. Se evaluó el efecto de la concentración del NaOH y la relación sólido/líquido (S/L). Los resultados indican que el rendimiento más alto es de 875.16 gAH/kg de leonardita empleando 4% de sólidos y una concentración de 0.5 M del agente extractante. La importancia en el rendimiento óptimo del proceso y el aprovechamiento de recursos naturales locales (leonardita) en términos de costos y sostenibilidad, son esenciales para el desarrollo de soluciones que beneficien tanto a los agricultores como al medio ambiente.