Composites materials like jute/epoxy exhibit high hardness and are considered as difficult-to-machine materials. As a result, alternatives to conventional machining become essential to post-process the composites. Accordingly, due to its non-thermal nature, abrasive water jet machining has recently come to be seen as one of the most promising machining methods for composite materials. In the current study, the impact of machining parameters such as traverse speed (TS), standoff distance (SOD) and abrasive mass flow rate (MFR) on machined surface roughness (Ra) has been investigated. In addition, the optimum combination of process parameters to machine a jute fiber-reinforced polymer composite with minimum Ra is predicted. The experimental results are analyzed using Taguchi and Response Surface Methodology (RSM) approaches to determine the optimum set of process parameters to achieve the lowest roughness values. Without making any changes in the machining conditions, the optimum set of values is determined for two conditions by reinforcing the fiber with 45° inclination and 90° inclination. The results reflect the different optimum combinations for each fiber inclination. For 45° fiber inclination, to achieve the minimum Ra value, the predicted combination is TS = 30 mm/min, SOD = 2 mm and MFR = 0.35 kg/min. When the fiber inclination is 90°, the predicted optimum combination is TS = 25 mm/min, SOD = 2 mm, and MFR = 0.35 kg/min. It is evident from the results that the optimum combination will be changed according to the machining conditions as well as material properties. The results confirm the effect of fiber orientation on surface roughness. The specimen with 45° fiber inclination produces a lower Ra with an average of 4.116 µm, and the specimen with 90° fiber inclination generates a higher Ra with an average of 4.961 µm.

Introduction: Among alloys of medium-carbon and high-strength steel, EN 24 steel is characterised by its nickel-chromium-molybdenum composition. EN 24 steel is highly suitable for application in heavy-duty projects due to its notable resilience to damage, especially when exposed to low temperatures. With the objective of minimising surface irregularities, this research endeavours to enhance the milling process of EN 24 steel by employing coated tungsten carbide (WC) tool inserts.Methods: Feed rate, cutting speed, depth of cut, and cutting fluid are all crucial process factors in the experimental investigation. Four distinct levels are applied to each factor. The research utilises the Design of Experiments (DOE)-based Central Composite Design of Response Surface Methodology. To predict output parameters, mathematical models are developed utilising analysis of variance (ANOVA) for optimisation purposes.Results and discussions: Through the utilisation of multi-objective optimisation, the optimal combination for tungsten carbide inserts was determined, which provided surface irregularities of 0.301 µm. Cutting speed (CS) of 149.507 m/min, feed rate (FR) of 340.27 mm/min, depth of cut (DOC) of 0.599 mm, and cutting fluid (CF) of 12.50 L/min are the optimal parameters. The surface morphologies of the machined workpiece at particular parameter values can be discerned through scanning electron microscope (SEM) analysis, yielding significant insights. The optimal parameters that have been identified provide practical recommendations for improving the milling method of EN 24 steel when tungsten carbide inserts are utilised. Understanding the milling process in its entirety is facilitated by SEM analysis of surface morphologies and microstructures under particular cutting conditions. The morphology and surface irregularities of the machined workpiece are evaluated using profilometry, which provides additional insight into surface integrity. The discourse investigates the potential applications and implications of the results, as well as suggests directions for further study concerning the enhancement of milling processes for similar steel alloys.