In order to provide more effective treatment strategies for the rapid healing of diabetic wounds, novel therapeutic approaches need to be developed. The therapeutic potential of peroxisome proliferator-activated receptor-γ (PPAR-γ) agonist pioglitazone hydrochloride (PHR) in two different release kinetic scenarios, burst release and sustained release, was investigated and compared with in vitro and in vivo tests as potential wound healing dressings. PHR-loaded fibrous mats were successfully fabricated using polyvinyl-pyrrolidone and polycaprolactone by scalable pressurized gyration. The results indicated that PHR-loaded fibrous mats expedited diabetic wound healing in type-1 diabetic rats and did not show any cytotoxic effect on NIH/3T3 (mouse embryo fibroblast) cells, albeit with different release kinetics and efficacies. The wound healing effects of fibrous mats are presented with histological and biochemical evaluations. PHR-loaded fibrous mats improved neutrophil infiltration, oedema, and inflammation and increased epidermal regeneration and fibroblast proliferation, but the formation of hair follicles and completely improved oedema were observed only in the sustained release form. Thus, topical administration of PPAR-γ agonist in sustained release form has high potential for the treatment of diabetic wounds in inflammatory and proliferative phases of healing with high bioavailability and fewer systemic side effects.

The fabrication of polymeric micro/nanofibers is gaining attention due to their use in an array of applications including tissue engineering scaffolds, nanosensors, and fiber-reinforced composites. Despite their versatile nature, polymeric fibers are widely underutilized due to the lack of reliable, large-scale production techniques. Upon the discovery of centrifugal spinning and, recently, pressurized gyration techniques, new research directions have emerged. Here, we report a comprehensive study detailing the optimal conditions to significantly improve the morphology, homogeneity, and yield of fibers of varying diameters. A series of polymeric fibers was created using a 21 wt. % solution of polyethylene oxide in distilled water and the fluid behavior was monitored inside a transparent reservoir using a high-speed camera. Fabrication of the fibers took less than 1 s. Using centrifugal spinning, we studied the formation of the fibers at three different rotational speeds, and for pressurized gyration, one rotational speed was studied with three different nitrogen gas pressures. Using the pressurized gyration technique at a gas pressure of 0.3 MPa, there was significant improvement in the production yield of the fibers. We found a strong correlation between the variation of pressure and the rate of the solution leaving the reservoir with the improved morphology of the fibers. The use of reduced power techniques, like centrifugal spinning and pressured gyration, to yield high-quality nonwoven nanofibers and microfibers in large quantities is important due to their use in rapidly expanding markets.

This review focuses on the effects on the environment due to the production of polymer‐solvent solutions and the manufacture of polymeric fibers of thicknesses from a nanometer up to a millimeter using these solutions. The most common polymeric fiber manufacture methods are reviewed based on their effects on the environment, particularly from the use of hazardous materials and energy consumption. Published literature is utilized to analyze and quantify energy consumption of the manufacturing methods electrospinning, phase separation, self‐assembly, template synthesis, drawing and pressurized gyration. The results show that during the manufacturing stage of the lifecycle of polymeric fibers, pressurized gyration is more environmentally efficient primarily due to its mass‐producing features and fast processing of polymeric solutions into fibers, it also works best with water‐based solutions. Further green alternatives are described such as the use of sustainable polymers and solvents to enhance the environmental benefit. Overall, it is shown that the most effective method of curbing the environmental impact of manufacturing polymeric fibers is the use of nontoxic, water‐soluble polymers along with the evasion of toxic solvents.